氧化铜/二氧化硅多孔复合材料的制备及其对亚甲基蓝的吸附性能

doi:10.3724/SP.J.1095.2014.30543

摘要/Abstract

摘要： 采用聚乙二醇（PEG）为模板，通过溶胶凝胶法-水热法制备出CuO/SiO2多孔复合材料，使用FTIR、HRTEM、XRD和BET等技术手段对目标产物进行了表征；研究添加CuO质量及反应温度等反应条件对复合材料的孔结构特征的影响。用目标产物作为吸附材料，研究了其对有机染料亚甲基蓝的吸附性能，结果表明，CuO/SiO2多孔复合材料对亚甲基蓝具有良好的吸附效果，尤其是含CuO质量分数为15%的样品在用量0.015 g、体系pH=9、搅拌时间为2 h的条件下，对10 mL亚甲基蓝（4 mg/L）的去除率最高可达97.17％。对吸附的过程和机理进行了初步探讨。

关键词: 溶胶凝胶法-水热法, 复合材料, 多孔材料, 吸附

Abstract: Mesoporous silica and its copper oxide doped composite materials were synthesized by sol-gel and hydrothermal methods, using polyethylene glycol(PEG) as template. The target products were characterized by FTIR, HRTEM, XRD, BET and so on. The influences of reaction condition, such as copper oxide quality and reaction temperature, on porous structure were investigated in details. The samples used as adsorption material for adsorption of methylene blue(MB) in wastewater were studied. CuO/SiO2 mesoporous oxide composite has good absorbability of MB. The maximum removal rate reaches 97.17% for 10 mL of 4 mg/L MB solution at pH 9 in the presence of 0.015 g sorbent. The process and mechanism of adsorption were also studied.

Key words: sol-gel-hydrothermal method, composites, porous material, adsorption

中图分类号:

O635.2

吴中正, 朱维菊, 王冬梅, 李村, 吴振玉. 氧化铜/二氧化硅多孔复合材料的制备及其对亚甲基蓝的吸附性能[J]. 应用化学, DOI: 10.3724/SP.J.1095.2014.30543.

WU Zhongzheng, ZHU Weiju, WANG Dongmei, LI Cun*, WU Zhenyu. Preparation of Copper Oxide-Silica Porous Composites and Its Adsorption of Methylene Blue[J]. Chinese Journal of Applied Chemistry, DOI: 10.3724/SP.J.1095.2014.30543.

参考文献

[1] LI Jiazhen. Treatment of Dyes, Dyeing Industrial Wastewater[M]. Beijing:Chemical Industry Press,2003:74(in Chinese).

李家珍. 染料、染色工业废水处理[M]. 北京:化学工业出版社,2003:74.

[2] LIU Rongzhan,LI Zhiguo,LIU Xuli,et al. The Textile Dyeing and Finishing of Industrial Wastewater Pollutants Recycling and Wastewater Treatment[J]. J Knitting Ind,2004,(5):115-120(in Chinese).

柳荣展,李志国,刘绪利,等. 纺织染整工业废水污染物回收与废水处理[J]. 针织工业,2004,(5):115-120.

[3] JIAO Xinting,LI Xiaodong,LIU Guowen. Carbon Nanotubes on the Methylene Blue Adsorption Performance Study[J]. J Safety Environ,2007,7(3):44-47(in Chinese).

焦新亭,李晓东,刘国文. 碳纳米管对亚甲基蓝的吸附性能研究[J]. 安全与环境学报,2007,7(3):44-47.

[4] LIANG Zhirong. Dye Wastewater Present Situation and the Progress of Physical and Chemical Treatment Technology[J]. J Sichuan Environ,2003,22(6):25-29(in Chinese).

梁志荣. 染料废水物理化学处理技术的现状与进展[J]. 四川环境,2003,22(6):25-29.

[5] LI Guifang,MENG Fanping. Sewage Sludge on the Adsorption Decolorization of Dye Wastewater Treatment Performance Research[J]. J Ocean Univ China,2005,35(1):91-94(in Chinese).

李桂芳,孟范平. 污水污泥对染料废水的吸附脱色性能研究[J]. 中国海洋大学学报,2005,35(1):91-94.

[6] Ryong R,Sang H J,Michal K,et al. Ordered Mesoporous Carbons[J]. Adv Mater,2001,13(9):677-680.

[7] Jinwoo L,Jaeyun K,Taeghwan H. Recent Progress in the Synthesis of Porous Carbon Materials[J]. Adv Mater,2006,18:2073 2094.

[8] Liang C D,Li Z J,Dai S. Mesoporous Carbon Materials:Synthesis and Modification[J]. Angew Chem Int Ed,2008,47(20):3696-3717.

[9] Wan Y,Shi Y F,Zhao D Y. Supramolecular Aggregates as Templates:Ordered Mesoporous Polymers and Carbons[J]. Chem Mater,2008,20(3):932-945.

[10] Zhao D Y,Feng J L,Huo Q S,et al. Triblock Copolymer Syntheses of Mesoporous Silica with Periodic 50 to 300 Angstrom Pores[J]. Science,1998,279:548-552.

[11] Ulrike C,Ferdi S. Ordered Mesoporous Materials[J]. Micropor Mesopor Mater,1999,27:131-149.

[12] Oscar A A,Andrea R B,Maria L M,et al. Synthesis and Characterization of SBA-3, SBA-15, and SBA-1 nanostructured catalytic materials[J]. J Colloid Interface Sci,2007,315:184-190.

[13] Patiparn P,Satoshi T. Selective Adsorption of Nonionic Surfactant on Hexagonal Mesoporous Silicates(HMSs) in the Presence of Ionic Dyes[J]. Water Res,2006,40:3177-3184.

[14] Manuela C,Elisa M,Loretta S,et al. Synthesis and Structural Characterization of MSU-type Silica tin Molecular Sieves:Post-synthesis Grafting of Tin Chlorides[J]. Micropor Mesopor Mater,2006,91:261-267.

[15] Liang X,Li J H,Lin Q C,et al. Synthesis and Characterization of Mesoporous Mn/Al-SBA-15 and Its Catalytic Activity for NO Reduction with Ammonia[J]. Catal Commun,2007,8:1901-1904.

[16] TAO HongLiang,YU Guiyu,YANG Nanru,et al. Preparation of Sol-gel Process without Support Gamma Al2O3 Membrane[J]. Bull Chinese Ceram Soc,1994,15(1):26-29(in Chinese).

陶洪亮，余桂郁，杨南如，等. Sol-gel工艺制备无支撑γ-Al2O3分离膜[J]. 硅酸盐通报,1994,15(1):26-29.

[17] WANG Juan,ZHANG Changrui,FENG Jian,et al. Influence of Polyethylene Glycol on Properties of Nano Porous Silicon Dioxide Thin Film[J]. J Inorg Mater,2005,3(2):435-437.

王娟，张长瑞，冯坚，等. 聚乙二醇对纳米多孔二氧化硅薄膜性能的影响[J]. 无机材料学报,2005,3(2):435-437.

[18] Toupance T,Kermarec M,Louis C. Metal Particle Size in Silica-supported Copper Catalysts. Influence of the Conditions of Preparation and of Thermal Pretreatments[J]. J Phys Chem B,2000,104(5):965-972.

[19] Chao K J,Wu C N,Chang A S,et al. The Study of MCM-41 Molecular Sieves by Energy-filtering TEM[J]. Micropor Mesopor Mater,1999,27:287-295.

[20] Mehmetd,Mahir A,Aydm T,et al. Kinetics and Mechanism of Removal of Methylene Blue by Adsorption onto Perlite[J]. J Hazard Mater,2004,(B109):141-148.

[21] LI Jiangtao,ZHENG Tao. Research of Mesoporous Carbon Materials on the Adsorption Properties of Methylene Blue[J]. J Xi′an College Arts Sci:Nat Sci Ed,2010,13(1):49-53(in Chinese).

李江涛,郑涛. 介孔炭材料对亚甲基兰的吸附特性研究[J]. 西安文理学院学报:自然科学版,2010,13(1):49-53.

[22] LIU Zhuannian,WANG Nianqin. The Mechanism of Superfine Fly Ash Adsorption of Methylene Blue[J]. Ion Exchange Adsorpt,2008,24(6):535-543(in Chinese).

刘转年,王念秦. 超细粉煤灰吸附亚甲基蓝的机理研究[J]. 离子交换与吸附,2008,24(6):535-543.

[23] Senth I S,Vardaraja P R,et al. Adsorption of Methylene Blue onto Jute Fiber Carbon:Kinetics and Equilibrium Studies[J]. J Colloid Interface Sci,2005,284:78-82.