基于甲氧基柱[5]芳烃的聚丙烯酸酯有机膜对对硝基苯衍生物的吸附行为

doi:10.11944/j.issn.1000-0518.2019.01.180054

摘要/Abstract

摘要：

柱芳烃是一类有别于冠醚、杯芳烃、葫芦脲等的柱状大环分子,具有独特的富电子空腔和口腔的可修饰性。它们可以包结多种有机污染物,对有机污染物的吸附和脱除具有广泛的应用前景。本文通过核磁共振和紫外滴定的方法首先研究了对硝基苯衍生物与甲氧基柱[5]芳烃(MeP5A)的包结行为,测定了包结常数。在此基础上,将MeP5A物理混合到聚丙烯酸酯(PA)乳液中,首先制备了甲氧基柱[5]芳烃/聚丙烯酸酯(MeP5A/PA)共混乳液,然后通过静电纺丝技术,得到了MeP5A/PA纳米纤维膜。采用红外光谱、扫描电子显微镜对MeP5A/PA纳米纤维膜的结构和形貌进行了表征。将MeP5A/PA纳米纤维膜用于4种对硝基苯衍生物的吸附实验。结果表明,对硝基苯乙腈显示出与MeP5A最强的包结作用,其K_a=(6.0±0.3)×10² L/mol,PA膜中引入MeP5A,增大了吸附量,但并未改变纤维状形貌。 MeP5A/PA纳米纤维膜的最佳吸附平衡时间为2 h,且MeP5A/PA纳米纤维膜中MeP5A的含量越高,吸附量越大。但当吸附溶液中MeP5A浓度达到4 mmol/L时(对应的膜中含有的MeP5A物质的量为1.4×10^-2 mmol),其吸附基本达到平衡,继续增加MeP5A物质的量,其吸附量变化不大。

关键词: 甲氧基柱[5]芳烃, 包结常数, 纳米纤维膜, 吸附

Abstract:

Pillararenes are columnar macrocyclic molecules that are different from crown ethers, calixarenes, and cucurbiturils, and have unique electron-rich cavities and modifiable mouth cavities. They can contain a variety of organic pollutants, and have broad application prospects for the adsorption and removal of organic pollutants. In this paper, the complexation of p-nitrobenzene derivatives with 1,4-dimethoxy pillar[5]arenes(MeP5A) was studied by nuclear magnetic resonance and ultraviolet titration, and the inclusion constant was determined. On this basis, MeP5A was physically mixed into polyacrylate(PA) emulsion to prepare the MeP5A/polyacrylate(MeP5A/PA) blending emulsion. Then, the blending emulsion was made into the MeP5A/PA nanofiber membrane by the electrospinning technology. The structure and morphology of the MeP5A/PA nanofiber membrane were characterized by infrared spectroscopy and scanning electron microscopy. The MeP5A/PA nanofiber membrane was used for adsorption of four kinds of p-nitrobenzene derivatives. The results reveal that p-nitrophenylacetonitrile holds the strongest complexation intensity with MeP5A[K_a=(6.0±0.3)×10² L/mol]. The introduction of MeP5A into the PA nanofiber membrane increases the adsorption capacity but does not change the fibrous morphology. The optimum adsorption equilibrium time of MeP5A/PA nanofiber membranes is 2 h, and the higher the content of MeP5A in MeP5A/PA nanofiber membranes, the larger the adsorption capacity. When the concentration of MeP5A in the adsorbed solution reaches 4 mmol/L(the corresponding MeP5A mole in the membrane is 1.4×10^-2 mmol), the adsorption equilibrium is reached. Then the content of MeP5A continues to increase, and the adsorption capacity does not change much.

Key words: dimethoxy pillar[5]arenes, inclusion constants, nanofiber membrane, adsorption

夏冬冬, 侯亚奇, 潘倩霞, 何子慧, 杨建哲, 汪海波. 基于甲氧基柱[5]芳烃的聚丙烯酸酯有机膜对对硝基苯衍生物的吸附行为[J]. 应用化学, 2019, 36(1): 24-33.

XIA Dongdong, HOU Yaqi, PAN Qianxia, HE Zihui, YANG Jianzhe, WANG Haibo. Adsorption of p-Nitrobenzene Derivatives by Polyacrylate Organic Membranes Based on 1,4-Dimethoxy Pillar[5]arenes[J]. Chinese Journal of Applied Chemistry, 2019, 36(1): 24-33.

参考文献

[1]	Cao Y,Li Y,Hu X Y,et al. Supramolecular Nanoparticles Constructed by DOX-Based Prodrug with Water-Soluble Pillar[6]arene for Self-catalyzed Rapid Drug Release[J]. Chem Mater,2015,27(3):1110-1119.
[2]	Cao Y,Hu X Y,Li Y,et al. Multistimuli-Responsive Supramolecular Vesicles Based on Water-Soluble Pillar[6]arene and Saint Complexation for Controllable Drug Release[J]. J Am Chem Soc,2014,136(30):10762-10769.
[3]	Zhou J,Chen M,Diao G W.Synthesis of the First Amphiphilic Pillar[6]Arene and Its Enzyme-Responsive Self-assembly in Water[J]. Chem Commun,2014,50(80):11954-11956.
[4]	Walsh M A,Walter S R,Bevan K H,et al. Phenylacetylene One-Dimensional Nanostructures on the Si(100)-2 x1:H Surface[J]. J Am Chem Soc,2010,132(9):3013-3019.
[5]	Si W,Xin P Y,Li Z T,et al. Tubular Unimolecular Transmembrane Channels:Construction Strategy and Transport Activities[J]. Acc Chem Res,2015,48(6):1612-1619.
[6]	Niu Z,Huang F,Gibson H W.Supramolecular AA-BB-Type Linear Polymers with Relatively High Molecular Weights via the Self-Assembly of Bis(m-phenylene)-32-Crown-10 Cryptands and a Bisparaquat Derivative[J]. J Am Chem Soc,2011,133(9):2836-2839.
[7]	Wang S L,Wang Y L,Chen Z X,et al. The Marriage of Endo-Cavity and Exo-Wall Complexation Provides a Facile Strategy for Supramolecular Polymerization[J]. Chem Commun,2015,51(16):3434-3437.
[8]	Li C J.Pillararene-Based Supramolecular Polymers:From Molecular Recognition to Polymeric Aggregates[J]. Chem Commun,2014,50(83):12420-12433.
[9]	Hu X Y,Wu X,Wang S,et al. Pillar[5]arene-Based Supramolecular Polypseudorotaxane Polymer Networks Constructed by Orthogonal Self-Assembly[J]. Polym Chem,2013,4(16):4292-4297.
[10]	Liang Z Q,Du J J,Sun L B,et al. Design and Synthesis of Two Porous Metal-Organic Frameworks with NBO and AGW Topologies Showing High CO2 Adsorption Capacity[J]. Inorg Chem,2013,52(19):10720-10722.
[11]	Jin Y H,Voss B A,Jin A,et al. Highly CO2-Selective Organic Molecular Cages:What Determines the CO2 Selectivity[J]. J Am Chem Soc,2011,133(17):6650-6658.
[12]	Jie K C,Zhou Y J,Yao Y,et al. CO2-Responsive Pillar[5]arene-Based Molecular Recognition in Water:Establishment and Application in Gas-Controlled Self-Assembly and Release[J]. J Am Chem Soc,2015,137(33):10472-10475.
[13]	Jie K C,Yao Y,Chi X,et al. A CO2-Responsive Pillar[5]arene:Synthesis and Self-assembly in Water[J]. Chem Commun,2014,50(41):5503-5505.
[14]	Tan L L,Li H W,Zhou Y,et al. Zn2+-Triggered Drug Release from Biocompatible Zirconium MOFs Equipped with Supramolecular Gates[J]. Small,2015,11(31):3807-3813.
[15]	Tan L L,Li H W,Tao Y,et al. Pillar[5]arene-Based Supramolecular Organic Frameworks for Highly Selective CO2-Capture at Ambient Conditions[J]. Adv Mater,2014,26(41):7027-7031.
[16]	Ogoshi T,Takashima S,Yamagishi T A.Molecular Recognition with Microporous Multilayer Films Prepared by Layer-by-Layer Assembly of Pillar[5]arenes[J]. J Am Chem Soc,2015,137(34):10962-10964.
[17]	Xue M,Yang Y,Chi X,et al. Pillararenes, A New Class of Macrocycles for Supramolecular Chemistry[J]. Acc Chem Res,2012,45(8):1294-1308.
[18]	Zhang W,Chen M,Diao G W.Electrospinning β-Cyclodextrin/Poly(vinyl alcohol) Nano-brous Membrane for Molecular Capture[J]. Carbohydr Polym,2011,86(3):1410-1416.
[19]	Hossain M F,Gong R H,Rigout M.Preparation and Characterization of Poly(ethylene oxide)-Loaded Hydroxypropyl-β-Cyclodextrin Nanofibers[J]. Polym Adv Technol,2015,26(9):1184-1188.
[20]	Ogoshi T,Kanai S,Fujinami S,et al. Para-bridged Symmetrical Pillar[5]arenes:Their Lewis Acid Catalyzed Synthesis and Host-Guest Property[J]. J Am Chem Soc,2008,130(15):5022-5023.
[21]	Zhu K,Li S,Wang F,et al. Anion-Controlled Ion-Pair Recognition of Paraquat by a Bis(m-phenylene)-32-crown-10 Derivative Heteroditopic Host[J]. J Org Chem,2009,74(3):1322-1328
[22]	Ogoshi T,Hashizume M,Yamagishi T A,et al. Synthesis, Conformational and Host Guest Properties of Water-Soluble Pillar[5]arene[J]. Chem Commun,2010,46(21):3708 3710.
[23]	Ogoshi T,Nishida Y,Yamagishi T,et al. Polypseudorotaxane Constructed from Pillar[5]arene and Viologen Polymer[J]. Macromolecules,2010,43(7): 3145 3147.
[24]	Hu X B,Chen L,Si W,et al. Pillar[5]arene Decaamine:Synthesis, Encapsulation of Very Long Linear Diacids and Formation of Ion Pair-Stopped [2]Rotaxanes[J]. Chem Commun,2011,47(16):4694-4696.