固相法合成苯胺与邻甲氧基苯胺共聚物及其性能

吐尔逊·阿不都热依木*,如仙古丽·加玛力,吐尼沙古丽·阿吾提,司马义·努尔拉,许峰,邵伟伟   

  1. (石油天然气精细化工教育部和自治区重点实验室，新疆大学化学化工学院 乌鲁木齐 830046)
  • 收稿日期:2011-11-21 修回日期:2012-02-12 出版日期:2012-10-10 发布日期:2012-10-10
  • 通讯作者: 吐尔逊·阿不都热依木，副教授; Tel/Fax:0991-8583575; E-mail:tursunabdir@sina.com.cn; 研究方向：光电活性高分子材料
  • 基金资助:
    国家自然科学基金资助项目(20964004)，石油天然气精细化工教育部和自治区重点实验室开放课题(XJDX0908-2009-03)

Solid-state Synthesis and Properties of Copolymers of Aniline and o-Methoxyaniline

Tursun Abdiryim*, Ruxangul Jamal, Tunsagul Awut, Ismayil Nurulla, XU Feng, SHAO Weiwei   

  1. (Key Laboratory of Oil and Gas Fine Chemicals,Ministry of Education and Xinjiang Uyghur Autonomous
    Region,College of Chemistry and Chemical Engineering,Xinjiang University,Urumqi 830046,China)
  • Received:2011-11-21 Revised:2012-02-12 Published:2012-10-10 Online:2012-10-10

PDF

1023

被引次数

1

摘要： 以苯胺和邻甲氧基苯胺为单体，甲磺酸为掺杂酸，用固相法合成了甲磺酸掺杂苯胺与邻甲氧基苯胺共聚物。 通过红外光谱、紫外可见吸收光谱、X射线衍射、透射电子显微镜、循环伏安和电导率等对共聚物进行了结构表征和性能测试。 结果表明，不同摩尔比的苯胺与邻甲氧基苯胺共聚物处于中间氧化态，随邻甲氧基苯胺含量的增大，共聚物的掺杂率降低。 共聚物具有较高的结晶性和纤维状形貌，当苯胺与邻甲氧基苯胺摩尔比为1∶1时，具有较高的电化学活性,其导电率为1.65 S/cm。

关键词: 固相法合成, 共聚物, 苯胺, 邻甲氧基苯胺

Abstract: Copolymers of aniline and o-methoxyaniline were synthesized by solid-state polymerization method using methanesulphonic acid as the doping acid. The resultant copolymers were characterized by FTIR, UV-Vis, TEM, X-ray diffraction, cyclic voltammetry and conductivity measurements. The results showed that the copolymers prepared under different aniline and o-methoxyaniline molar ratios displayed an emeraldine salt phase, and the doping degree of copolymers decreased with increasing content of o-methoxyaniline in monomers. The as-prepared copolymers had a high crystallinity and displayed a fibrillar morphology. The copolymer prepared under the molar ratio of 1∶1, exhibited a higher electrochemical activity than the others, and its conductivity was 1.65 S/cm.

Key words: solid-state synthesis, copolymer, aniline, o-methoxyaniline