不同形貌氧化锌的微波水热法制备及其光催化性能

doi:10.11944/j.issn.1000-0518.2017.02.160161

摘要/Abstract

摘要：

采用微波水热法在乙二醇的辅助下,制备出一系列不同形貌的氧化锌(ZnO)纳米/微米颗粒。扫描电子显微镜测试结果表明,乙二醇的加入量对样品的形貌有着非常显著的影响,通过控制乙二醇的加入量,可以得到不规则片状、六方棱柱孪晶、梭子形和球形等形貌的ZnO纳米/微米颗粒。从微波反应器检测压力结果可以看出,乙二醇的加入量对反应体系的压力影响非常显著,这起到了调控纳米晶生长速度的效果进而得到不同形貌的样品。在此基础上,系统测试了样品在氙灯照射下光催化降解罗丹明B的能力,结果表明,乙二醇加入量大于12 mL时的球状样品光催化效率要远高于其他样品,在50 min内能完成对罗丹明B的降解。

关键词: 氧化锌, 微波水热, 乙二醇, 光催化, 罗丹明B

Abstract:

ZnO with various morphologies has been obtained by microwave hydrothermal method with the assistance of ethylene glycol(EG). By adjusting the concentration of EG in the system, the morphology of sample can be tuned from irregular disks to twin crystal rods, to shuttle shape, and finally to sphere shape. It is founded that the concentration of EG plays an important role in adjusting system pressure, which significantly influence the reaction speed and final shape of products. The photocatalytic activity of as-prepared ZnO with different morphologies in aqueous solution was investigated by bleaching dye rhodamine B under Xe lamp. The sphere shape sample possesses the most efficient photocatalytic properties, which can completely photodegradate rhodamine B in 50 min.

Key words: ZnO, microwave hydrothermal, ethylene glycol, photocatalytic, rhodamine B

王松, 李阳, 李飞, 程晓红. 不同形貌氧化锌的微波水热法制备及其光催化性能[J]. 应用化学, 2017, 34(2): 220-224.

WANG Song, LI Yang, LI Fei, CHENG Xiaohong. Microwave Hydrothermal Synthesis and Photocatalytic Properties of ZnO Nano-/Microparticles[J]. Chinese Journal of Applied Chemistry, 2017, 34(2): 220-224.

参考文献

[1]	Fujishima A,Honda K. Electrochemical Photolysis of Water at a Semiconductor Electrode[J]. Nature,1972,238:37-38.
[2]	Greene L E,Law M,Goldberger J,et al.Low-Temperature Wafer-Scale Production of ZnO Nanowire Arrays[J]. Angew Chem Int Ed,2003,42(26):3139-3142.
[3]	Özgür Ü,Alivov Y I,Liu C,et al. A Comprehensive Review of ZnO Materials and Devices[J]. J Appl Phys,2005,98(4):041301-041301-103.
[4]	Zhang Q,Deneau C S,Zhou X,et al.ZnO Nanostructures for Dye-Sensitized Solar Cells[J]. Adv Mater,2009,21(41):4087-4108.
[5]	Yu W L,Zhang J F,Peng T Y. New Insight into the Enhanced Photocatalytic Activity of N-, C- and S-doped ZnO Photocatalysts[J]. Appl Catal B Environ,2016,181(12):220-227.
[6]	Wang H,Li G,Jia L,et al.Controllable Preferential-Etching Synthesis and Photocatalytic Activity of Porous ZnO Nanotubes[J]. J Phys Chem C,2008,112(31):11738-11743.
[7]	Kansal S K,Singh M,Sud D. Studies on Photodegradation of Two Commercial Dyes in Aqueous Phase Using Different Photocatalysts[J]. J Hazard Mater,2007,141(3):581-590.
[8]	Sobana N,Swaminathan M. The Effect of Operational Parameters on the Photocatalytic Degradation of Acid Red 18 by ZnO[J]. Sep Purif Technol,2007,56(1):101-107.
[9]	Houšková V,Štengl V,Bakardjieva S,et al.Nanostructure Materials for Destruction of Warfare Agents and Eco-toxins Prepared by Homogeneous Hydrolysis with Thioacetamide:Part 1.Zinc Oxide[J]. J Phys Chem Solids,2007,68(5/6):716-720.
[10]	Kaneco S,Katsumata H,Suzuki T,et al.Solar Photo-catalytic Degradation of Endocrine Disruptor Di-n-butyl Phthalate in Aqueous Solution Using Zinc Oxide[J]. Bull Catal Soc India,2007,6(3):22-33.
[11]	Zhang Q,Bai W. Synthesis and Growth Mechanism of Macroscopic ZnO Nanocombs and Nanobelts[J]. Vacuum,2011,86(4):398-402.
[12]	Duan H F,He H P,Sun L W,et al.Indium-doped ZnO Nanowires with Infrequent Growth Orientation, Rough Surfaces and Low-density Surface Traps[J]. Nanoscale Res Lett,2013,8(1):493-493.
[13]	Liu Z,Lei E,Jing Y,et al.Growth of ZnO Nanorods by Aqueous Solution Method with Electrodeposited ZnO Seed Layers[J]. Appl Surf Sci,2009,255(12):6415-6420.
[14]	Yue S,Yan Z,Shi Y,et al.Synthesis of Zinc Oxide Nanotubes within Ultrathin Anodic Aluminum Oxide Membrane by Sol-gel Method[J]. Mater Lett,2013,98(5):246-249.
[15]	Lou Z,Deng J,Wang L,et al.Toluene and Ethanol Sensing Performances of Pristine and Pdo-decorated Flower-like ZnO Structures[J]. Sens Actuators B,2013,176(1):323-329.
[16]	Li Z Q,Ding Y,Xiong Y J,et al.Room-temperature Surface-erosion Route to ZnO Nanorod Arrays and Urchin-like Assemblies[J]. Chemistry,2004,10(22):5823-5828.
[17]	Yang P,Yan H,Mao S,et al.Controlled Growth of ZnO Nanowires and Their Optical Properties[J]. Adv Funct Mater,2002,12(5):323-331.
[18]	WANG Yan,TAN Guoqiang,MIAO Hongyan,et al.Preparation of Zinc Oxide Nano Powder by Microwave Hydrothermal Method and Its Photocatalytic Property[J]. Rare Met Mater Eng,2011,(S1):32-35(in Chinese). 王艳,谈国强,苗鸿雁,等. 微波水热法制备氧化锌纳米粉体及其光催化性能[J]. 稀有金属材料与工程,2011,(S1):32-35.
[19]	WANG Ruizhi,WANG Zhenzhen,ZHANG Ming,et al.Room-temperature Synthesis and Photocatalytic Activity of Lamella Flower-like ZnO[J]. Chinese J Appl Chem,2014,31(3):316-322(in Chinese). 王瑞枝,王真真,张明,等. 室温合成片层花状氧化锌及其光催化[J]. 应用化学,2014,31(3):316-322.
[20]	LIU Zili,ZHU Yucong,WANG Kui,et al.Sythesis of Zinc Oxide with Dandelions Shape and Its Photocatalytic Propertie[J]. J He'nan Normal Univ(Nat Sci),2015,(1):63-68(in Chinese). 刘自力,朱郁葱,王魁,等. 蒲公英状氧化锌的合成及光催化性能研究[J]. 河南师范大学学报:自然科学版,2015,(1):63-68.