Study on Complexes of Natural Rubber Latex Blended with Hydrophilic Organosiloxane

JIANG Guo-Min1, ZHAO Qun1, GU Xue-Fang1, ZHANG Yu2, WANG Xu-Rong3, GE Cun-Wang1*   

  1. (1.School of Chemistry and Chemical Engineering,Nantong University,Nantong 226007;
    2.Jiangsu Key Laboratory for Biomaterials and Devices,Southeast University,Nanjing;
    3.Ke Guang New Material Limited Company of Nantong,Nantong)
  • Received:2009-03-04 Revised:2009-05-10 Published:2010-02-10 Online:2010-02-10

Abstract:

The natural rubber latexes were blended with hydrophilic organosiloxane KGF-903 for the improvement of its performance. The effect of the content of organosiloxane on blended natural rubber latex was investigated through mechanical, antiaging, hydrophilic and morphological measurement. It indicated that the mechanical and antiaging properties were improved with the addition of organosiloxane at an optimal content of 1.5%, at which the tensile strengths of improved natural rubber before and after the aging were increased by 37% and 44%, respectively. The elongations at break were monotonously increased with the addition of organosilicone at a saturated content of 3%, at which the elongations at break were improved by 57% and 50%. The more the content of organosilicone, the smaller the contact angle of the nature rubber latex. SEM analysis indicated that the dispersive state of nature rubber latex was improved with the addition of organosilicone. The two batch formulas were adopted in the manufacture of urethral catheter with an optimal addition of 1.5% of KGF-903. The catheters were obtained with smooth surface, finer evenness, moderate hardness and favorable yield of latex sacculus. The separation forces between connector and the interface of conical drainage  as well as the tensile force between gas loading filler and drainage tube were improved, which guaranteed the safety of Foley latex in clinic use.

Key words: nature rubber latex, organosiloxane, blend, mechanical and antiaging properties, hydrophilicity