CoO-CuO-SiO2三元系统着色涂层的研究

长山   

  1. 内蒙古师范大学配位化学研究所, 呼和浩特 010022
  • 收稿日期:1990-11-10 修回日期:1991-05-24 出版日期:1992-02-10 发布日期:1992-02-10

THE COLORED FILM OF TERTIARY SYSTEM CoO-CuO-SiO2

Chang Shan   

  1. Institute of Coordination Chemistry, Inner Mongolia Normal University, Huhhot 010022
  • Received:1990-11-10 Revised:1991-05-24 Published:1992-02-10 Online:1992-02-10

PDF

403

摘要： 利用溶胶-凝胶法制备反射膜、抗反射膜以及着色涂层的研究近年来较引人注目。山本雄二等报道过CoO-SiO2、CuO-SiO2、NiO-SiO2等二元系统着色涂层,涂层的颜色基本上与其中所包含的有色离子颜色相同。本文采用溶胶-凝胶法制备了CoO-CuO-SiO2着色涂层,得到了具有Co2+和Cu2+的混合颜色的着色涂层,并确定了该体系的成膜区。

关键词: 溶胶-凝胶法, 涂膜, 硅酸盐

Abstract: The colored film of CoO-CuO-SiO2 system was prepared by sol-gel method. The effect of several factors, such as concentration of oxides, viscosity of coating solution, heating temperature and heating time on optical transmittance of the film were examined and the compositions for homogeneous glass films were determined. The homogeneous films can be produced only from the system containing more than 50 mol% SiO2. Both Co2+, and Cu2+ ions were shown not to take part in network bonds formation.

Key words: sol-gel method, coating film, silicate