单一基质白光荧光粉Na3Sc2(PO4)3∶Tm3+,Dy3+的合成及发光性质

doi:10.19894/j.issn.1000-0518.210119

摘要/Abstract

摘要： 采用高温固相法成功制备了Na₃Sc_2-x-y(PO₄)₃∶xTm³⁺,yDy³⁺荧光粉,利用X射线衍射仪、扫描电子显微镜和荧光光谱仪对荧光粉进行了物相、形貌和发光性能进行了表征。在Na₃Sc₂(PO₄)₃∶0.06Tm³⁺,yDy³⁺荧光粉中,物质的量分数6%的Tm³⁺和6%的Dy³⁺在360 nm激发下呈现出白光发射,其发射光谱在460~685 nm范围内存在Tm³⁺位于457 nm的特征发射峰,对应于Tm³⁺的³H₆→¹D₂跃迁,以及Dy³⁺位于483、577和672 nm处的3个特征发射峰,分别对应于Dy³⁺的⁴F_9/2→⁶H_15/2、⁴F_9/2→⁶H_13/2和⁴F_9/2→⁶H_11/2的跃迁。观测到Na₃Sc₂(PO₄)₃∶Tm³⁺荧光粉的发射光谱与Na₃Sc₂(PO₄)₃∶Dy³⁺的激发光谱有较好的重叠,且Tm³⁺的荧光寿命随Dy³⁺浓度的增加逐渐降低,因此在Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺荧光粉中存在Tm³⁺向Dy³⁺的能量传递。利用Dexter和Reisfeld近似分析了能量转移机制,发现从Tm³⁺到Dy³⁺的能量传递临界距离为1.6 nm,能量传递过程是通过偶极-偶极相互作用进行的。 Na₃Sc₂(PO₄)₃∶0.06Tm³⁺,0.06Dy³⁺荧光粉具有较好的耐受热猝灭性能,在423、473和523 K时的发射强度分别为298 K时发射强度的97.6%、89.2%和78.6%。随着Dy³⁺浓度的增加,Na₃Sc₂(PO₄)₃∶0.06Tm³⁺,yDy³⁺荧光粉的发光颜色由蓝色转变为白色,再由白色变黄色。 Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺荧光粉作为一种可调色或单相白光荧光粉在发光二极管上具有潜在的应用前景。

关键词: 白光荧光粉, 耐热稳定性, 发光二极管

Abstract: A series of NSPO∶0.06Tm³⁺, yDy³⁺(y=0~0.10) phosphors were synthesized by the high-temperature solid-state method, and their phase, morphology and luminescent properties of the phosphors were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and fluorescence spectrometer. Under the excitation of 360 nm, the photoluminescence (PL) spectrum of Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺ shows the Tm³⁺ characteristic emission peak at 457 nm and three characteristic emission peaks of Dy³⁺ at 483, 577, and 672 nm, respectively. There is an energy transfer from Tm³⁺ to Dy³⁺ ion in Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺ phosphor due to the good overlap between the emission spectrum of Na₃Sc₂(PO₄)₃∶Tm³⁺ and the excitation spectrum of Na₃Sc₂(PO₄)₃∶Dy³⁺, which is further confirmed by the fluorescence lifetime decrease of Tm³⁺ ion with the increase of Dy³⁺ concentration. The process of energy transfer is via dipole-dipole interaction which is confirmed by applying Dexter and Reisfeld's theory. By increasing the Dy³⁺ concentration, the color coordinates of the Na₃Sc₂(PO₄)₃∶0.06Tm³⁺,yDy³⁺ phosphors could be adjusted from blue to white, and then to yellow. The Na₃Sc₂(PO₄)₃∶0.06Tm³⁺,0.06Dy³⁺ phosphor shows fairly good resistance to thermal quenching with a high preservation of the emission intensities of 97.6%, 89.2% and 78.6% at 423, 473 and 523 K, respectively. These results suggest that the Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺ phosphors have potential applications as the color-tunable or a single-phase white emitting phosphor in white light-emitting diodes (LEDs).

Key words: White phosphor, Thermal quenching, Light-emitting diodes

中图分类号:

O611.4

王森, 庞然, 李达, 李成宇, 张洪杰. 单一基质白光荧光粉Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺的合成及发光性质[J]. 应用化学, 2021, 38(11): 1469-1478.

WANG Sen, PANG Ran, LI Da, LI Cheng-Yu, ZHANG Hong-Jie. Synthesis and Luminescence Properties of a Single-Phase White-Emitting and Tunable Color Phosphor Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺[J]. Chinese Journal of Applied Chemistry, 2021, 38(11): 1469-1478.

参考文献

[1] PHILIPP P, PETER J S, WOLFGANG S. A revolution in lighting[J]. Nat Mater, 2015, 14(5): 454-458.
[2] HUANG X Y. New red phosphors enable white LEDs to show both high luminous efficacy and color rendering index[J]. Sci Bull, 2019, 64(13): 879-880.
[3] CHO J, PARK J H, KIM J K, et al. White light-emitting diodes: history, progress, and future[J]. Laser Photon Rev, 2017, 11(2): 1600147-1600164.
[4] HOUSER K W, WEI M C, DAVID A, et al. Review of measures for light-source color rendition and considerations for a two-measure system for characterizing color rendition[J]. Opt Express, 2013, 21(8): 10393-10411.
[5] PIAO X Q, TAKASHI H, HIROMASA H, et al. Characterization and luminescence properties of Sr₂Si₅N₈∶Eu²⁺ phosphor for white light-emitting-diode illumination[J]. Appl Phys Lett, 2006, 88(16): 161908-161910.
[6] XIA Z G, XU Z H, CHEN M Y, et al. Recent developments in the new inorganic solid-state LED phosphors[J]. Dalton Trans, 2016, 28(28): 11201-11582.
[7] YANG C T, XIE L J, XIAO Q L, et al. Ba_1-xSr_xMgSiO₄∶Eu²⁺,Mn²⁺: a novel tunable single-matrix tricolor phosphor for WLED[J]. J Rare Earth, 2012, 30(2): 110-113.
[8] GOLJA D, DEJENE F. Structural and photoluminescence characteristics of the single-host green-light-emitting T-phase Ba_1.3Ca_0.7SiO₄∶Tb³⁺ phosphors for LEDs[J]. Chem Phys Lett, 2020, 16: 137122-137131.
[9] FAN B, ZHOU W X, QI S M, et al. Eu³⁺-doped NaYGeO₄: a novel red-emitting phosphors for ultraviolet or blue chips excited white LEDs[J]. J Solid State Chem, 2020, 283: 121158-121164.
[10] WANG B, KONG Y C, CHEN Z K, et al. Thermal stability and photoluminescence of Mn²⁺ activated green-emitting feldspar phosphor SrAl₂Si₂O₈∶Mn²⁺ for wide gamut w-LED backlight[J]. Opt Mater, 2020, 99(1): 109535
[11] ZHANG Y F, XIONG J, SHEN D Y, et al. Tunable luminescence evolution and ET behavior of Na₃Sc₂(PO₄)₃∶Ce³⁺/Tb³⁺/Eu³⁺ phosphors[J]. RSC Adv, 2019, 9: 1270-1277.
[12] WU H Y, LI H M, JIANG L H, et al. Synthesis, structure and optical properties of novel thermally robust Dy³⁺-doped Ca₉Sc(PO₄)₇ phosphors for NUV-excited white LEDs[J]. J Rare Earth, 2021, 39(3): 277-283.
[13] ZHANG Y, ZHOU T S, LIU H, et al. Structure and luminescence properties of Sr₉La(PO₄)₅(SiO₄)F₂∶Dy³⁺ single-component white-emitting phosphor for n-UV w-LEDs[J]. Opt Mater, 2018, 84: 689-693.
[14] WANG Q, XIE M L, MIN X, et al. Synthesis, structural, and luminescence properties of Biocl∶Dy³⁺ single component white-light-emitting phosphor for n-UV w-LEDs[J]. Chem Phys Lett, 2019, 727(16): 72-77.
[15] FERHI M, TOUMI S, HORCHANI-NAIFER K, et al. Single phase GdPO₄∶Dy³⁺ microspheres blue, yellow and white light emitting phosphor[J]. J Alloys Compd, 2017, 714(15): 144-153.
[16] KIM J S, JEON P E, PARK Y H, et al. White-light generation through ultraviolet-emitting diode and white-emitting phosphor[J]. Appl Phys Lett, 2004, 85(17): 3696-3698.
[17] YANG F G, QIAO L, REN H K, et al. Synthesis and luminescence properties of color-tunable Dy³⁺/Eu³⁺∶CeAlON phosphors[J]. Ceram Int, 2017, 43(11): 8406-8410.
[18] HAN B, DAI Y Z, ZHANG J, et al. Development of near-ultraviolet-excitable single-phase white-light-emitting phosphor KBaY(BO₃)₂∶Ce³⁺,Dy³⁺ for phosphor-converted white light-emitting-diodes[J]. Ceram Int, 2018, 44(12): 14803-14810.
[19] LU M, ZHU C F, CHEN Z T, et al. Ce³⁺ and Dy³⁺ doped Ca₃(P_1-xB_xO₄)₂ phosphors for white light-emitting applications[J]. J Alloys Compd, 2019, 775: 1044-1051.
[20] RAMBABU U, BALAJI T, ANNAPURNA K, et al. Fluorescence spectra of Tm³⁺-doped rare earth oxychloride powder phosphors[J]. Mater Chem Phys, 1996, 43(2): 195-198.
[21] HWANG M H, LEE E Y, HONG S H, et al. Preparation and luminescent properties of Ca₅(PO₄)₃Cl∶Eu²⁺ phosphors by a solid-state reaction method[J]. J Electrochem Soc, 2009, 156(7): J185-J188.
[22] CHIANG C H, LU Y M, FANG Y C, et al. Effects of deionized water modification of raw materials on properties of Ca₆BaP₄O₁₇∶Eu²⁺ phosphate phosphors[J]. Ceram Int, 2018, 44(15): 18376-18381.
[23] QIAO J W, NING L X, MOLOKEEV M S, et al. Eu²⁺ site preferences in the mixed cation K₂BaCa(PO₄)₂ and thermally stable luminescence[J]. J Am Ceram Soc, 2018, 140(30): 9730-9736.
[24] TKACHEV V V, PONOMAREV V I, ATOVMYAN L O. Crystal structure of the solid electrolyte Na₃Sc₂(PO₄)₃ in the temperature range 27-350 ℃[J]. J Struct Chem, 1984, 25(1): 111-116.
[25] WANG X C, ZHAO Z Y, WU Q S, et al. Structure, photoluminescence and abnormal thermal quenching behavior of Eu²⁺-doped Na₃Sc₂(PO₄)₃: a novel blue-emitting phosphor for n-UV LEDs[J]. J Mater Chem C Mater, 2016, 4(37): 8795-8801.
[26] KIM Y H, ARUNKUMAR P, KIM B Y, et al. A zero-thermal-quenching phosphor[J]. Nat Mater, 2017, 16(5): 543-551.
[27] KACZMAREK S M, TSUBOI T J, BOULON G. Valency states of Yb, Eu, Dy and Ti ions in Li₂B₄O₇ glasses[J]. Opt Mater, 2003, 22(4): 303-310.
[28] YE R G, CUI Z G, HUA Y J, et al. Eu²⁺/Dy³⁺ co-doped white light emission glass ceramics under UV light excitation[J]. J Non Cryst Solids, 2011, 357(11/12/13): 2282-2285.
[29] LAHOZ F, MARTIN I R, MENDEZ-RAMOS J, et al. Dopant distribution in a Tm³⁺-Yb³⁺ codoped silica based glass ceramic:an infrared-laser induced upconversion study[J]. J Chem Phys, 2004, 120(13): 6180-6190.
[30] YANG W J, LUO L Y, CHEN T M, et al. Luminescence and ET of Eu- and Mn-coactivated CaAl₂Si₂O₈ as a potential phosphor for white-light UVLED[J]. Chem Mater, 2005, 17(15): 3883-3888.
[31] DEXTER D L, SCHULMAN J H. Theory of concentration quenching in inorganic phosphors[J]. J Chem Phys, 1954, 22(6): 1063-1070.
[32] FONGER W H, STRUCK C W. Eu³⁺ ⁵D resonance quenching to the charge-transfer states in Y₂O₂S, La₂O₂S, and LaOCl[J]. J Chem Phys, 1970, 52(12): 6364-6372.

单一基质白光荧光粉Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺的合成及发光性质

Synthesis and Luminescence Properties of a Single-Phase White-Emitting and Tunable Color Phosphor Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 14

编辑推荐

Metrics

本文评价

[1]	陈栎岩, 赵梓茗, 陶金琪, 张玉贞, 程刚, 沈云军. 单、双核含双硫配体金属有机铂磷光材料合成及其OLED应用[J]. 应用化学, 2023, 40(2): 236-244.
[2]	孟丹, 郑开元, 陈珊珊, 卓钊龙, 王丽丽. 硅、氮共掺杂碳点荧光粉的制备及发光性能[J]. 应用化学, 2022, 39(11): 1766-1773.
[3]	郭海泉, 杨正华, 高连勋. 光敏聚酰亚胺光刻胶研究进展[J]. 应用化学, 2021, 38(9): 1119-1137.
[4]	王森, 庞然, 李达, 李成宇, 张洪杰. 单一基质白光荧光粉Na₃Sc₂(PO₄)₃∶Tm³⁺,Dy³⁺的合成及发光性质[J]. 应用化学, 2021, 38(11): 0-0.
[5]	黄国斌, 骆登峰, 张茂升. 多色高发光效率CsPbX₃(X=Cl,Br,I)钙钛矿量子点的制备及其在发光二极管中的应用[J]. 应用化学, 2019, 36(8): 932-938.
[6]	黄国斌, 骆登峰, 张茂升. 多色高发光效率CsPbX₃(X=Cl,Br,I)钙钛矿量子点的制备及其在发光二极管中的应用[J]. 应用化学, 2019, 36(8): 0-.
[7]	霍冉,吴雨萱,杨煜,朴树清,张治城,肖佶海,史翎. 石墨烯电子器件的研究进展[J]. 应用化学, 2019, 36(3): 245-258.
[8]	李飞,夏志国. 固态照明用稀土荧光粉和无机量子点:机遇与挑战[J]. 应用化学, 2018, 35(8): 859-870.
[9]	袁廷,孟婷,李淑花,范楼珍. 基于磷光材料的电致发光二极管研究进展[J]. 应用化学, 2018, 35(8): 871-880.
[10]	李帅龙, 刘小明, 唐星华, 冯景春, 谢伟杰. Ba₃Y(PO₄)₃:Dy³⁺,Eu³⁺单基质白光荧光粉的制备与发光性能[J]. 应用化学, 2017, 34(10): 1186-1194.
[11]	解荣军,周天亮,高桥向星,广崎尚登. 在发光二极管背光源上极具应用前景的Beta-sialon (Si_6-_zAl_zO_zN_8-_z):Eu²⁺窄带绿色荧光粉[J]. 应用化学, 2016, 33(8): 855-866.
[12]	代岩峰,张智强,刘一鹏,马东阁. 无间隔层结构的高效率荧光/磷光混合型白光有机发光二极管[J]. 应用化学, 2015, 32(10): 1139-1145.
[13]	杨君维, 王淑萌, 丁军桥, 王利祥. 螺芴/2,8-S,S-二氧-二苯并噻吩共聚物的合成与性能[J]. 应用化学, 2014, 31(10): 1156-1163.
[14]	史常生, 陈江山, 马东阁. 超薄铝/碳酸锂修饰氧化铟锡阴极制备蓝色磷光反转底发光有机发光二极管[J]. 应用化学, 2012, 29(12): 1412-1416.