可见光响应Gd-N-TiO2纳米光催化剂的溶胶-水热制备及表征

doi:10.3724/SP.J.1095.2013.20302

摘要/Abstract

摘要： 利用溶胶-水热法制备了未掺杂、N掺杂、Gd掺杂和Gd-N共掺杂TiO2纳米光催化剂，以甲基橙(MO)溶液在紫外光和可见光照射下的光催化脱色评价其光活性；采用XRD、XPS、BET、UV-Vis和PL分析技术表征样品的物理化学性能，探讨Gd-N共掺杂对TiO2光活性的影响机制。结果表明，Gd掺杂能有效抑制光生e-/h+的复合，提高光量子效率；抑制TiO2晶粒生长，改善样品表面织构特性，明显提高紫外光活性。 N掺杂窄化TiO2带隙，拓宽光吸收范围至可见光区，从而提高了可见光活性。 Gd-N共掺杂进一步窄化带隙增加可见光吸收，减小晶粒尺寸，改善样品的表面织构特性，增强织构的热稳定性。与单掺杂样品相比，Gd-N-TiO2在可见光照射下对MO的光催化脱色活性进一步提高，这归因于Gd-N共掺杂的协同效应。

关键词: 纳米TiO2, Gd-N共掺杂, 溶胶-水热, 可见光响应, 协同效应

Abstract: Un-doped, N-doped, Gd-doped and Gd-N-codoped TiO2 nano-photocatalysts were successfully prepared by a sol-hydrothermal method. Their photocatalytic activities were evaluated by photocatalytic decoloration of methyl orange dye in aqueous solution under UV and visible light irradiation, respectively. The physicochemical properties of as-prepared samples were characterized by XRD, XPS, BET, UV-Vis and PL analytic techniques. The effect of Gd-N-codoping on the photoactivity of TiO2 was also discussed. The results showed that Gd-doping could effectively inhibit the recombination of photogenerated electronhole pairs, then enhancing photo quantum efficiency. Gd-doping could inhibit the growth of crystalline size and improve the surface textural properties. Therefore, the UV photoactivity was obviously enhanced by Gd-doping. N-doping could make the absorption edge red-shift to visible light range by narrowing the electronic band structure, which enhanced the visible light photoactivity. Gd-N-codoping could further increase the absorption to visible light by narrowing the electronic band structure, and further decrease the crystalline size and improve the surface textural properties, therefore increasing the thermal stability. Compared to the single-doped TiO2, Gd-N-TiO2 significantly improved the photoactivity for decoloring methyl orange in aqueous solution under visible light irradiation, which was ascribed to the synergetic effect of Gd-N-codoping.

Key words: nano-TiO2, Gd-N-codoping, sol-hydrothermal, visible light response, synergetic effect

中图分类号:

O643.3

王庆元, 姜洪泉, 李井申, 王巧凤, 李振宇. 可见光响应Gd-N-TiO₂纳米光催化剂的溶胶-水热制备及表征[J]. 应用化学, DOI: 10.3724/SP.J.1095.2013.20302.

WANG Qingyuan, JIANG Hongquan*, LI Jingshen, WANG Qiaofeng, LI Zhenyu. Sol-hydrothermal Preparation and Characterization of Gd-N-TiO₂ Nano-photocatalyst with Visible Light Response[J]. Chinese Journal of Applied Chemistry, DOI: 10.3724/SP.J.1095.2013.20302.

参考文献

[1] Fujishima A, Honda K. Electrochemical photolysis of water at a semiconductor electrode[J]. Nature, 1972, 238:37-38.
[2] Hu S Z, Li F Y, Fan Z P. The influence of preparation method, nitrogen source, and post-treatment on the photo-catalytic activity and stability of N-doped TiO2 nanopowder[J]. J. Hazard. Mater., 2011, 196:248-254.
[3] Wang P H, Yap P S, Lim T T. C-N-S tridoped TiO2 for photocatalytic degradation of tetracycline under visi-ble-light irradiation[J]. Appl. Catal. A: Chem., 2011, 399:252-261.
[4] WANG Chengying, JIANG Hongquan, LI Jingshen, et al. Preparation and visible-light responsive mechanism of nanoscale TiO2-yNx photocatalyst[J]. Chinese J Appl. Chem., 2010, 27(12):1413-1418(in Chinese).
王城英，姜洪泉，李井申，等. TiO2-yNx纳米光催化剂的制备及其可见光响应机理[J]. 应用化学，2010 27(12):1413-1418.
[5] Silva A M T, Silva C G, et al. Ce-doped TiO2 for photocatalytic degradation of chlorophenol[J]. Catal. Today, 2009, 144:13-18.
[6] Xiao Q, Si Z C, et al. Characterization and photocatalytic activity of Sm3+-doped TiO2 nanocrystalline prepared by low temperature combustion method[J]. J Alloys Compd, 2008, 450:426-431.
[7] LUO Sha, LIU Shouxin. Preparation and Characterization of Gadolinium-doped TiO2 /Activated Carbon Fibre Composite[J]. Chinese J Appl. Chem., 2011, 28(1):66-71(in Chinese).
罗沙, 刘守新. Gd 掺杂TiO2 /活性炭纤维复合材料的制备及表征[J].应用化学, 2011, 28(1):66-71.
[8] Zhang R Y, Guo Y, Jin C, et al. Novel thermally stable phosphorus-doped TiO2 photocatalyst synthesized by hy-drolysis of TiCl4 [J]. J. Mol. Cataly. A, 2010, 319: 46-51.
[9] Asahi R, Morikawa T, Ohwaki T, et al. Visible-light photocatalysis in nitrogen-doped titanium oxides [J]. Science, 2001, 293:269-271.
[10] Zhang H R, Tan K Q, Zheng H W, et al. preparation, characterization and photocatalytic activity of TiO2 codoped with yttrium and nitrogen[J]. Mater. Chem. Phys., 2011, 125:156-160.
[11] Cong Y, Tian B Z, Zhang J L. Improving the thermal stability and photocatalytic activity of nanosized titanium dioxide via La3+ and N co-doping[J]. Appl. Catal. B: Environ., 2011, 101:376-381.
[12] Wang C, Ao Y H , Wang P F, et al. Preparation of cerium and nitrogen co-doped titania hollow spheres with en-hanced visible light photocatalytic performance[J]. Powder Technol., 2011, 210:203-207.
[13] Yang J, Dai J, Li J T. Synthesis, characterization and degradation of Bisphenol A using Pr, N co-doped TiO2 with highly visible light activity[J]. Appl. Surf. Sci., 2011, 275: 8965-8973.
[14] Ma Y F, Zhang J L, Tian B Z, et al. Synthesis and characterization of thermally stable Sm,N co-doped TiO2 with highly visible light activity[J]. J. Hazard. Mater., 2010, 182:386-393.
[15] Xu J J, Y H Ao, Fu D G, et al. A simple route for the preparation of Eu, N-codoped TiO2 nanoparticles with en-hanced visible light-induced photocatalytic activity. J. Colloid Interface Sci, 2008, 328: 447-451.
[16] Liu H J, Liu G G, Xie G H, et al. Gd3+, N-codoped trititanate nanotubes: Preparation, characterization and photocatalytic activity[J]. Appl. Surf. Sci., 2011, 275: 3728-3732.
[17] Ma Y F, Xing M Y, Zhang J L, et al. Synthesis of well ordered mesoporous Yb, N co-doped TiO2 with superior visible photocatalytic activity[J]. Microporous Mesoporous Mater., 2012, 156:145-152.
[18] Li H B, Liu G C, Chen S G, et al. Novel Fe doped mesoporous TiO2 microspheres: Ultrasonic-hydrothermal syn-thesis, characterization, and photocatalytic properties[J]. Physica E, 2010, 42:1844-1849.

可见光响应Gd-N-TiO₂纳米光催化剂的溶胶-水热制备及表征

Sol-hydrothermal Preparation and Characterization of Gd-N-TiO₂ Nano-photocatalyst with Visible Light Response

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	李颖, 张云, 林良良, 许虎君. N‑月桂酰基甲基丙氨酸钠三元复配体系的协同效应[J]. 应用化学, 2022, 39(8): 1262-1273.
[2]	徐迪, 戴力, 姚文志, 杨光瑞, 王海荣, 宋鹏飞, 朱岩松. 烯烃聚合催化剂的研究进展[J]. 应用化学, 2022, 39(3): 355-373.
[3]	毕一飘, 宫雪, 杨发, 阮明波, 宋平, 徐维林. 多价MnO_x/C电催化剂用于高效氮还原反应[J]. 应用化学, 2020, 37(9): 1048-1055.
[4]	王凤平, 胡晓强, 丁言伟, 李杰兰, 张薇. 山梨酸钾与Zn²⁺在NaCl溶液中对Q235钢的缓蚀协同作用[J]. 应用化学, 2020, 37(8): 960-968.
[5]	范亮姣, 田玉芹, 钱钦, 陈雷, 郭宏伟, 辛爱渊, 侯万国. 黄原胶和瓜尔胶混合溶液及其硼砂交联体系的流变性能[J]. 应用化学, 2020, 37(5): 531-540.
[6]	陈琪, 费霞, 何琴琴, 武其亮, 何兵, 刘雪霆. 铽负载介孔二氧化钛的制备、表征和协同效应[J]. 应用化学, 2014, 31(10): 1222-1228.
[7]	杨丽君, 刘雪岩, 姜鑫, 李莹, 常怀春, 张蕾. 纳米TiO₂去除氟离子的性能[J]. 应用化学, 2012, 29(11): 1278-1285.
[8]	文雯, 高晓亚, 张爱平, 宋志英, 孙彦平. 纳米TiO₂光催化氧化对胃癌细胞周期的影响[J]. 应用化学, 2012, 29(06): 663-667.
[9]	王城英, 姜洪泉, 李井申, 卢智宇, 闫盼盼. TiO_2-yN_x纳米光催化剂的制备及其可见光响应机理[J]. 应用化学, 2010, 27(12): 1413-1418.
[10]	李向红, 邓书端, 付惠, 木冠南. 稀土Ce⁴⁺和香兰素在H₃PO₄介质中对钢的缓蚀协同效应[J]. 应用化学, 2010, 27(07): 836-841.
[11]	张蕾, 赵中原, 金燕利, 李绮. 甲基丙烯酸丁酯在纳米TiO2表面的原位接枝[J]. 应用化学, 2009, 26(5): 547-550.
[12]	过家好, 何晓英, 蔡生民, 郭敏, 陈秀英, 彭孝军. 甲醇对三甲川菁染料敏化TiO2纳米晶电极的影响[J]. 应用化学, 2008, 25(7): 753-758.
[13]	李俊华, 张复兴, 王剑秋, 曾荣英, 邓培红, 彭运林, 陈晓东. 纳米TiO2修饰碳糊电极伏安法测量痕量铟[J]. 应用化学, 2008, 25(6): 718-721.
[14]	孙鹂, 邹海峰, 王成. 形貌可控表面修饰纳米级tio2的合成与表征[J]. 应用化学, 2007, 24(11): 1259-1262.
[15]	刘彦平, 杨志远. 改性纳米TiO2降解水中微量次甲基蓝的动力学研究[J]. 应用化学, 2006, 23(9): 1019-1022.