二乙基硅氧烷双苯并环丁烯的合成及其聚合物性能

黄学亮1.2,朱方华2,杨军校1,张林2*   

  1. (1.西南科技大学材料科学与工程学院 绵阳；2.中国工程物理研究院激光聚变研究中心 绵阳 621900)
  • 收稿日期:2010-07-22 修回日期:2010-10-15 出版日期:2011-06-10 发布日期:2011-06-10
  • 通讯作者: 张林，研究员; Tel/Fax:0816-2493148; E-mail:zhlmy@sina.com; 研究方向：功能材料开发及其应用
  • 基金资助:
    国家高技术研究发展计划项目“八六三”基金资助项目（2009AA8-441011）

Synthesis and Properties of Diethyl Tetramethyl Disiloxane Bisbenzocyclobutene and Its Polymer

HUANG Xueliang1,2, ZHU Fanghua2, YANG Junxiao1, ZHANG Lin2*   

  1. (1.School of Materials Science and Engineering,Southwest University of Science and Technology,Mianyang;
    2.Research Center of Laser Fusion,China Academy of Engineering Physics,Mianyang 621900)
  • Received:2010-07-22 Revised:2010-10-15 Published:2011-06-10 Online:2011-06-10
  • Contact: Zhang lin

PDF

2289

被引次数

7

摘要：

利用硅氢加成反应，以4-乙烯基苯并环丁烯(4-VBCB)和1,1,3,3-四甲基-1,3-二氢二硅氧烷（TMHS）为原料，一步法合成了二乙基硅氧烷双苯并环丁烯（DES-bis-BCB），并对以其为单体在热引发条件下生成的预聚体进行了结构表征。 利用原子力显微镜和热重分析对预聚体的成膜性能和热性能进行了分析。 结果显示，薄膜的均方根（RMS）糙度为0.53 nm，初始分解温度为390 ℃，表明二乙基硅氧烷双苯并环丁烯聚合物具有良好的成膜性能和优异的热稳定性能。

关键词: 双苯并环丁烯, 硅氢加成反应, 热性能, 成膜性能。

Abstract:

Hydrosilylation reaction of 4-vinylbenzocyclobutene(4-VBCB) with 1,1,3,3-tetramethyl-1,3-dihydro-disiloxane(TMHS) was employed to afford the monomer of diethyl tetramethyl disiloxane-bisbenzocyclobutene(DES-bis-BCB). The structures of DES-bis-BCB and the prepolymer prepared from DES-bis-BCB by thermal isomerization ring opening polymerization reaction were characterized and analyzed. The surface morphology and thermal stability of the films were investigated by atomic force microscopy(AFM) and thermogravimetric analysis(TGA), respectively. The results showed that the root-mean square(RMS) roughness was 0.53 nm, and the starting mass loss temperature was about 390 ℃. It indicated that DES-bis-BCB exhibited good film-forming property and excellent thermal stability.

Key words: bisbenzocyclobutene, hydrosilylation reaction, thermal properties, film-forming property.