燃料电池用侧链型磺化聚砜质子交换膜的性能

doi:10.11944/j.issn.1000-0518.2019.08.190013

摘要/Abstract

摘要：

在制备氯甲基化聚砜(CPS)的基础上,以1,2-二羟基苯-3,5-二磺酸钠为试剂,通过亲核取代反应制备一种侧链末端为磺酸基团的侧链型磺化聚砜(PS-BDS),并采用溶液浇注法制备相应的质子交换膜(PEM),研究温度对PEM性能的影响规律。结果表明,由于亲水基团远离疏水聚合物主链,该PEM能够形成亲水微区远离疏水微区的相分离结构,亲水区域对主链的影响较小,该PEM在高磺化度下仍能保持较好的尺寸稳定性,随着温度的升高,PEM的吸水率(WU)、吸水溶胀率(SW)和质子传导率(PC)升高,其中PS-BDS-4(离子交换容量为1.57 mmol/g)在25和85 ℃时的SW仅为22.1%和55.0%,甲醇的渗透率(DK)仅为10.17×10^-7 cm²/s,低于商业化的Nafion115(16.8×10^-7 cm²/s)和Nafion117(23.8×10^-7 cm²/s),表现出很好的综合性能。

关键词: 聚砜, 质子交换膜, 相分离, 尺寸稳定性

Abstract:

Chloromethylated polysulfones(CPS) was used as the precursors, and side chain type sulfonted polysulfone(PS-BDS) was obtained using disodium 1,2-dihydroxybenzene-3,5-disufonate as nucleophilic reagents. The corresponding proton exchange membranes(PEMs) were produced using solution casting method. The relationship between the temperature and properties of PEMs was studied. Since they have characteristic micro-phase separation structures by locating hydrophilic sulfonic acid group far away from hydrophobic main chain of PS, PEMs have excellent dimensional stability at high water sorption ratio. With the increase of temperature, the proton conductivity, the swelling ratio and the water sorption ratio increase. PS-BDS PEMs have comprehensive size stability and methanol permeability. The swelling ratio of PS-BDS-4 PEM is only 22.1% at 25 ℃ and 55.0% at 85 ℃. The methanol permeability is 9.94×10^-7 cm²/s at 25 ℃, lower than those of commercial Nafion115(16.8×10^-7 cm²/s) and Nafion117(23.8×10^-7 cm²/s) PEMs.

Key words: polysulfone, exchange membranesphase separation, dimensional stability

乔宗文, 陈涛. 燃料电池用侧链型磺化聚砜质子交换膜的性能[J]. 应用化学, 2019, 36(8): 917-923.

QIAO Zongwen, CHEN Tao. Properties of Side Chain Type Sulfonated Polysulfone Proton Exchange Membranes for Fuel Cells[J]. Chinese Journal of Applied Chemistry, 2019, 36(8): 917-923.

参考文献

[1]	Kima K,Junga B K,Koa T, et al. Polysulfones Containing Sulfonated Polytriazole Side Chains for Proton Exchange Membranes[J]. J Membr Sci,2018,554(15):232-243.
[2]	Liu D,Xu M Z,Fang M L, et al. Branched Comb-shaped Poly(arylene ether sulfone)s Containing Flexible Alkyl Imidazolium Side Chains as Anion Exchange Membranes[J]. J Mater Chem,2018,6:10879-10890.
[3]	Yan X M,Zhang C M,Dong Z W, et al. Amphiprotic Side-Chain Functionalization Constructing Highly Proton/Vanadium-Selective Transport Channels for High-Performance Membranes in Vanadium Redox Flow Batteries[J]. Appl Mater Interfaces,2018,10(38):32247-32255.
[4]	Li X,Zhao Y,Li W W, et al. Molecular Dynamics Simulation of Radiation Grafted FEP Films as Proton Exchange Membranes:Effects of the Side Chain Length[J]. Int J Hydrogen Energy,2017,42(50):29977-29987.
[5]	Han M M,Zhang G,Li M Y, et al. Sulfonated Poly(etheretherketone) Polybenzimidazole Oligomer/Epoxy Resin Composite Membranes in Situ Polymerization for Direct Methanol Fuel Cell Usages[J]. J Power Sources,2011,196:9916-9923.
[6]	QIAO Zongwen,YAN Xiaoqian.Properties of Naphthalenesulfonic Acid Type Polysulfone Proton Exchange Membrane[J]. Chem Res Appl,2018,30(12):1993-1998(in Chinese). 乔宗文,闫晓前. 萘磺酸型侧链磺化聚砜质子交换膜的性能[J]. 化学研究与应用,2018,30(12):1993-1998.
[7]	Kumar P,Dutta K,Das S, et al. Membrane Prepared by Incorporation of Crosslinked Sulfonated Polystyrene in the Blend of PVdF-co-HFP/Nafion[J]. Appl Energy,2014,123:66-74.
[8]	RONG Qian,GU Shuang,HE Gaohong, et al. Preparation and Performance of Sulfonated Polyether Ether/Ketone/Poly4-Vinylepyridine Acid-Base Composite Proton Exchange Membrane[J]. Polym Mater Sci Eng,2009,8:126-129(in Chinese). 荣倩,顾爽,贺高红,等. SPEEK/P4VP酸碱复合PEMs的制备与性能[J]. 高分子材料科学与工程,2009,8:126-129.
[9]	GONG Feixiang,QI Yonghong,XUE Qunxiang.Synthesis and Properties of Fluorinated Poly(arylene ether sulfone)s with Sulfonated Pentiptycene Pendants as Proton Exchange Membranes[J]. Chem J Chinese Univ,2014,35:433-439(in Chinese). 宫飞祥,齐永红,薛群翔. 含氟磺化双三蝶烯型聚芳醚砜PEMs的制备及性能[J]. 高等学校化学学报,2014,35:433-439.
[10]	Jin C H,Zhu X L,Zhang S, et al. Highly Conductive Flexible Alkylsulfonated Side Chains Poly(phthalazinone ether ketone)s for Proton Exchange Membranes[J]. Polymer,2018,148(18):269-277.
[11]	Zhang X L,Shi Q,Chen P, et al. Block Poly(arylene ether sulfone) Copolymers Tethering Aromatic Side-Chain Quaternary Ammonium as Anion Exchange Membranes[J]. Polym Chem,2018,9:699-711.
[12]	QIAO Zongwen,CHEN Tao.Effect of Side Chain Structure on Properties of Side Chain Type Sulfonated Polysulfone Proton Exchange Membranes[J]. Chem Bull,2019,82(5):457-462(in Chinese). 乔宗文,陈涛. 侧链结构对侧链型磺化聚砜质子交换膜性能的影响[J]. 化学通报,2019,82(5):457-462.
[13]	Liu D,Tao D,Ni J P, et al. Synthesis and Properties of Highly Branched Sulfonated Poly(arylene ether)s with Flexible Alkylsulfonated Side Chains as Proton Exchange Membranes[J]. J Mater Chem C,2016,4:1326-1335.
[14]	Pang J H,Shen K Z,Feng S N, et al. Polymer Electrolyte Membranes Based on Poly(arylene ether)s with Flexible Disulfophenyl Pendant[J]. J Power Sources,2014,263:59-65.
[15]	TAO Dan,XIANG Xiongzhi,WANG Lei.Synthsis and Characterization of Poly(arylene ether)s Proton Exchange Membranes with Sulfonic Groups Attached on Pendent Naphthyl Rings[J]. Acta Polym Sin,2014,3:326-332(in Chinese). 陶丹,向雄志,王雷. 磺酸基在侧链萘环上的磺化聚芳醚PEMs的制备与性能研究[J]. 高分子学报,2014,3:326-332.
[16]	Ekström H,Lafitte B,Ihonen J, et al. Evaluation of a Sulfophenylated Polysulfone Membrane in a Fuel Cell at 60 to 110 ℃[J]. Solid State Ionics,2007,178:959-966.
[17]	Zhang Y,Wan Y,Zhao C J, et al. Novel Side-Chain-Type Sulfonated Poly(arylene ether ketone) with Pendant Sulfoalkyl Groups for Direct Methanol Fuel Cells[J]. Polymer,2009,50:4471-4478.