秸秆预处理工艺对秸秆基人造板性能的影响

doi:10.11944/j.issn.1000-0518.2016.04.150278

摘要/Abstract

摘要：

随着木材工业的快速发展,以及木材原料的日益减少,利用农作物秸秆代替木材生产复合材料十分必要。本文以水稻秸秆为原料,以脲醛树脂为粘合剂,通过湿热法、偶联剂表面化学改性的方法,对秸秆表面进行改性,从而提高了树脂和秸秆之间的结合力,探索了水稻秸秆板的制作工艺。实验表明较好的制备工艺为:温度150 ℃,压强15 MPa,热压时间8 min,树脂胶粉和水的质量比为1:1,脲醛树脂胶含量为15%(质量分数),发现秸秆表面预处理采用γ-缩水甘油醚氧丙基三甲氧基硅烷(KH560)偶联剂后,所制得的秸秆板的诸多性能优于未经预处理及采用γ-氨丙基三乙氧基硅烷(KH550)进行改性后所制的秸秆板。

关键词: 秸秆, 表面改性, 脲醛树脂, 偶联剂

Abstract:

The renewable lignocellulosic sources for biocomposites have received much attention in recent years because of the shortage of forest resources. The surface of rice straw was pretreated through humid-heat and chemical modification by coupling reagent which could improve the adhesion capacity between urea formaldehyde resin and rice straw. Meanwhile, the process of fabricating straw board was explored in this paper. The experimental data shows that the straw boards with perfect properties are prepared under the temperature of 150 ℃, the pressure of 15 MPa, the hot pressing time of 8 min, the mass ratio of resin powder to water of 1:1, and the urea formaldehyde resin adhesive content of 15%(mass fraction). The straw boards prepared by 3-glycidyloxypropyltrimethoxysilane(KH560) as surface modification reagent show better properties than those by KH550 and untreated rice straw.

Key words: straw, surface modification, urea formaldehyde resin, coupling agent

靳璇, 李赢, 李新, 余志科, 张天宇, 丁重阳, 石刚. 秸秆预处理工艺对秸秆基人造板性能的影响[J]. 应用化学, 2016, 33(4): 430-435.

JIN Xuan, LI Ying, LI Xin, YU Zhike, ZHANG Tianyu, DING Zhongyang, SHI Gang. Effect of Pretreatment Methods of Rice Straw on Straw Board Properties[J]. Chinese Journal of Applied Chemistry, 2016, 33(4): 430-435.

参考文献

[1]	SUN Wanli,TAO Wenyi. Effect of Lignin and Hemicellulose on Enzymatic Hydrolysis of Cellulose from Rice Straw[J]. J Food Sci Biotechnol,2010,29(1):18-22(in Chinese). 孙万里,陶文沂. 木质素与半纤维素对稻草秸秆酶解的影响[J]. 食品与生物技术学报,2010,29(1):18-22.
[2]	Menezes E G T,Carmo J R,Alves J L F,et al. Optimization of Alkaline Pretreatment of Coffee Pulp for Production of Bioethanol[J]. Biotechnol Prog,2014,30(2):451-462.
[3]	ZHANG Qiang,MA Qi,XU Shengyun,et al.Study on the Degradation of β-Glucan of Corn Stalk by β-Glucanase[J]. J Food Sci Biotechnol,2009,28(6):828-831(in Chinese). 张强,马齐,徐升运,等.β-葡聚糖酶降解玉米秸秆中β-葡聚糖的工艺[J].食品与生物技术学报,2009,28(6):828-831.
[4]	Li Y,Ding X,Guo Y,et al.A New Method of Comprehensive Utilization of Rice Husk[J]. J Hazard Mater,2011,186(2/3):2151-2156.
[5]	GONG Guizhen,CAO Hong. Analysis of Petroleum Ether and Ethanol Extractable Species from Rice Straw[J]. Chinese J Appl Chem,2014,31(6):726-731(in Chinese). 宫贵贞,曹洪. 水稻秸秆石油醚和乙醇萃取物的组成分析[J]. 应用化学,2014,31(6):726-731.
[6]	NAN Yanyan,ZOU Hua,YAN Qun,et al.Elemental Study on the Biogas Anaerobic Fermentation with Crops Straw[J]. J Food Sci Biotechnol,2007,26(6):64-68(in Chinese). 南艳艳,邹华,严群,等. 秸秆厌氧发酵产沼气的初步研究[J]. 食品与生物技术学报,2007,26(6):64-68.
[7]	Mosier N,Wyman C,Dale B,et al.Features of Promising Technologies for Pretreatment of Lignocellulosic Biomass[J]. Bioresour Technol,2005,96(6):673-686.
[8]	FAN Jingjing,MA Deli,XI Yanru,et al.Laccase Production under Solid-State Fermentation of Wheat Straw and Its Degradation by Pycnoporus sanguineus SYBC-L12[J]. J Food Sci Biotechnol,2015,34(2):128-133(in Chinese). 范晶晶,马德丽,席艳茹,等. 血红密孔菌Pycnoporus Sanguineus SYBC-L12 固态发酵小麦秸秆产漆酶及其对小麦秸秆的降解作用[J]. 食品与生物技术学报,2015,34(2):128-133.
[9]	NU Dun,WANG Linshan,WANG Yuhong,et al.Modification of Rice Straw by Epichlorohy[J]. Chinese J Appl Chem,2005,22(9):1033-1035(in Chinese). 牛盾,王林山,王育红,等. 环氧氯丙烷改性稻草[J]. 应用化学,2005,22(9):1033-1035.
[10]	WANG Lulu,CAI Guolin,ZHU Dewei,et al.Effect of Ball Milling Pretreatment and Solid State Fermentation on the Feed Quality of Corn Straw[J]. J Food Sci Biotechnol,2014,33(11):1148-1153(in Chinese). 王璐璐,蔡国林,朱德伟,等. 球磨预处理和固态发酵对玉米秸秆饲用品质的影响[J]. 食品与生物技术学报,2014,33(11):1148-1153.
[11]	LIAN Hailan,ZHOU Dingguo,YOU Jixue. Studies on Layer Composites of Wheat Stalk and Their Adhesion Properties[J]. Chem Ind Forest Prod,2005,25(1):69-72(in Chinese). 连海兰,周定国,尤纪雪. 麦秸秆成分剖析及其胶合性能的研究[J]. 林产化学与工业,2005,25(1):69-72.
[12]	Liu Z M,Wang F H,Wang X M. Surface Structureand Dynamic Adhesive Wettability of Wheat Straw[J]. Wood Fiber Sci,2004,36(2):239-249.
[13]	Mo X Q,Cheng E Z,Wang D H,et al.Physical Properties of Medium-Density Wheat Straw Particleboard Using Different Adhesives[J]. Ind Crop Prod,2003,18(1):47-53.
[14]	WANG Lijuan,ZHANG Shuangbao. Present Situation and Problem of Wheat-Straw Board in China[J]. Wood Process Mach,2005,16(1):39-41 (in Chinese). 王莉娟,张双宝. 我国麦秸板的研究现状及其存在的问题[J]. 木材加工机械,2005,16(1):39-41.
[15]	Wasylciw W,Wang S G. Performance and Problems of Crop Straw Board and Bonding Technology of Urea-Formaldehyde Resin[J]. China Wood-based Panel,2001,(11):12-18(in Chinese). Wasylciw W,Wang S G. 农作物秸秆人造板性能、问题与脲醛树脂胶合技术[J]. 人造板通讯,2001,(11):12-18.
[16]	WANG Qi,LI Jining,SHI Yuliang. Influnce of Shaving Shape of Cornstalk Particle on the Physical and Mechanical Properties of Cornstalk Particleboard[J]. Agric Technol,2005,25(6):41-42 (in Chinese). 王琪,李济宁,史宇亮. 玉米秸秆刨花形态对刨花板物理性能的影响[J]. 农业与技术,2005,25(6):41-42.
[17]	ZHU Yun,SHEN Liming. The Density's Effect on the Physical Properties of the Rice Straw Fiberboard[J]. J Guangdong Univ Petrochem Technol,2013,23(4):53-55(in Chinese). 朱云,申黎明. 密度对稻秸秆纤维板物理性能的影响[J]. 广东石油化工学院学报,2013,23(4):53-55.
[18]	Blitz J P,Gun'ko V M,Samala R,et al. Mixed Bifunctional Surface-modified Silicas Using Tethered Aminofunctional Silane Catalysts[J]. Colloids Surf,A,2014,462(20):1-8.
[19]	Wang Y,Zhou C,Sun L,et al.One Step Synthesis of Boronic Acid Group Modified Silica Particles by the Aid of Epoxy Silanes[J]. Appl Surf Sci,2015,351(1):353-357.
[20]	LI Xuefeng,ZOU Dan,CHEN Qianwen,et al.Progress on Improving Compatatibility of Straw Fiber/Polymer Composites[J]. New Chem Mater,2014,42(7):30-32(in Chinese). 李学峰,邹丹,陈倩文,等. 秸秆/聚合物复合材料界面相容性的研究进展[J]. 化工新型材料,2014,42(7):30-32.