Chinese Journal of Applied Chemistry ›› 2020, Vol. 37 ›› Issue (1): 40-45.DOI: 10.11944/j.issn.1000-0518.2020.01.190153

• Full Papers • Previous Articles     Next Articles

Relationship Between the Concentration of Superabsorbent Resin and Its Adhesion Properties

LI Shuangshuangab,MA Ruib,LIU Fangb,FU Zhileib,PAN Geb,WANG Xiaoweib,XU Donghuab*(),XU Zhaohuac,SHI Tongfeib,HU Weia*()   

  1. aSchool of Chemical Engineering,Changchun University of Technology,Changchun 130012,China
    bState Key Laboratory of Polymer Physics and Chemistry,Changchun Institute ofApplied Chemistry,Chinese Acdemy of Sciences,Changchun 130022,China
    cJiangmen Polytechnic,Jiangmen,Guangdong 529090,China
  • Received:2019-05-24 Accepted:2019-09-03 Published:2020-01-08 Online:2020-01-08
  • Contact: XU Donghua,HU Wei
  • Supported by:
    Supported by the National Natural Science Foundation of China(No.21274152), Changchun Science and Technology Plan Science and Technology Innovation “Double Ten” Project Major Science and Technology Projects(No.17ss016), and Jiangmen Functional Materials and Coatings Key Laboratory(No.jiangke【2018】352)

Abstract:

The effect of the mass fraction of super absorbent resin on the adhesion of wood board was studied. The concentration range of the gel formed by the sample was determined by the rheological method and inverted experiment. The maximum water absorption ratio of the superabsorbent polymer was measured and the water absorption saturation concentration was determined. Through the simulation of the fire engine spray gun to the scene of the fire scene, the sample was sprayed to determine the adhesion performance of the gel on the fixed area of the board. The results show that the adhesion performance of the superabsorbent resin is related to its mass fraction. As the concentration increases, the adhesion performance of the sample increases. When the mass fraction of the superabsorbent resin sample reaches its gel mass fraction, the adhesion performance is greatly improved. When the increase is continued, the adhesion performance is increased to a small extent, and the adhesion layer falls off in a monolith due to the gravity.

Key words: superabsorbent polymer, mass fraction, adhesion performance, water absorption ratio