柱芳烃基多孔聚合物的制备及其吸附性能

doi:10.11944/j.issn.1000-0518.2019.10.190070

摘要/Abstract

摘要：

将柱[5]芳烃与1,3,5-三乙炔苯(TEB)通过Sonogashira偶联反应制备了一类新型多孔有机聚合物P[5]-TEB,进而通过脱甲基反应对其进行改性得到多羟基的多孔聚合物P[5]OH-TEB,对二者的物理化学性质和吸附性能进行研究。氮吸附测试表明,羟基的引入使P[5]OH-TEB的比表面积变大,同时引入微孔结构。染料吸附实验表明,两聚合物对亚甲基蓝吸附过程符合Langmuir模型,P[5]OH-TEB对亚甲基蓝有更大的吸附量;吸附动力学试验表明,吸附过程更符合拟二级动力学模型,属于化学吸附过程,改性之后P[5]OH-TEB有更快的吸附速率;选择性吸附实验表明,羟基引入聚合物后聚合物对阳离子染料的吸附性能提升,对阴离子染料的吸附效果变差。

关键词: 多孔有机聚合物, 柱芳烃, 染料吸附

Abstract:

A porous organic polymer containing pillar[5]arene and 1,3,5-trirthynylbenze(TEB), namely, P[5]-TEB, was synthesized by Sonogashira cross-coupling reaction, then a novel polyhydroxyl polymer P[5]OH-TEB was obtained by demethylation reaction from the former polymer. The physical and chemical properties as well as adsorption properties of the two porous organic polymers were studied. Nitrogen adsorption test showed that the specific surface area of P[5]OH-TEB increased with the introduction of hydroxyl group, and the microporous structure was also introduced. It was indicated by dye adsorption that the adsorption process of the two polymers for methylene blue was consistent with the Langmuir adsorption equation, from which P[5]OH-TEB had a greater adsorption capacity for methylene blue. The adsorption kinetics test indicated that the adsorption process was more suitable for the pseudo-secondary kinetics model and belonged to the chemical adsorption process and P[5]OH-TEB got a faster adsorption rate after modification. It was showed by selectivity adsorption that the polymer can absorb more cationic dyes and the adsorption was decreased to anionic dye after the introduction of hydroxyl group into the polymer.

Key words: porous organic polymers, pillararene, dye absorption

王星月, 张世越, 曲卫东, 贡卫涛, 宁桂玲. 柱芳烃基多孔聚合物的制备及其吸附性能[J]. 应用化学, 2019, 36(10): 1147-1154.

WANG Xingyue, ZHANG Shiyue, QU Weidong, GONG Weitao, NING Guiling. Synthesis of Pillar[5]arene-Based Porous Organic Polymers and Their Adsorption Properties[J]. Chinese Journal of Applied Chemistry, 2019, 36(10): 1147-1154.

参考文献

[1]	Chen S,Zhang J,Zhang C,et al. Equilibrium and Kinetic Studies of Methyl Orange and Methyl Violet Adsorption on Activated Carbon Derived from Phragmites australis[J]. Desalination,2010,252(1/3):149-156.
[2]	Crini G.Non-conventional Low-cost Adsorbents for Dye Removal:A Review[J]. Bioresour Technol,2006,97(9):1061-1085.
[3]	Mittal A,Malviya A,Kaur D,et al. Studies on the Adsorption Kinetics and Isotherms for the Removal and Rcovery of Methyl Orange from Wastewaters Using Waste Materials[J]. J Hazard Mater,2007,148(1/2):229-240.
[4]	XUE Yonggang,GUAN Song,DAI Xiaohu,et al. Research Progress of Membrane Separation Technology Used in Printing and Dyeing Wastewater Treatment and Reuse[J]. Text Dyeing Finish J,2014,36(5):26-31(in Chinese). 薛勇刚,官嵩,戴晓虎,等. 膜分离技术用于印染废水处理及回用的研究进展[J]. 染整技术,2014,36(5):26-31.
[5]	Kumar R,Ahmad R.Biosorption of Hazardous Crystal Violet Dye from Aqueous Solution onto Treated Ginger Waste(TGW)[J]. Desalination,2011,265(1/3):112-118.
[6]	Auta M,Hameed B H.Preparation of Waste Tea Activated Carbon Using Potassium Acetate as an Activating Agent for Adsorption of Acid Blue 25 Dye[J]. Chem Eng J,2011,171(2):502-509.
[7]	Asghar A,Abdul Raman A A,Wan Daud W M A. Advanced Oxidation Processes for in-situ Production of Hydrogen Peroxide/Hydroxyl Radical for Textile Wastewater Treatment:A Review[J]. J Cleaner Prod,2015,87:826-838.
[8]	Fu Z,Zhang Y,Wang X.Textiles Wastewater Treatment Using Anoxic Filter Bed and Biological Wriggle Bed-Ozone Biological Aerated Filter[J]. Bioresour Technol,2011,102(4):3748-3753.
[9]	AN Liancai,HAN Jiufang,ZHANG Yinghui,et al. Research and Application Progress on Porous Organic Polymers for Adsorption and Separation of Organic Pollutants in Water System[J]. Chinese J Appl Chem,2018,35(9):1019-1025(in Chinese). 安连财,韩久放,章应辉,等. 多孔有机聚合物吸附分离水体系中有机污染物研究和应用进展[J]. 应用化学,2018,35(9):1019-1025.
[10]	Wu D,Xu F,Sun B,et al. Design and Preparation of Porous Polymers[J]. Chem Rev,2012,112(7):3959-4015.
[11]	Dawson R,Cooper A I,Adams D J.Nanoporous Organic Polymer Networks[J]. Prog Polym Sci,2012,37(4):530-563.
[12]	Vincent G,Lukasz J W,Alkordi M,et al. Porous Organic Polymers with Anchored Aldehydes:A New Platform for Post-synthetic Amine Functionalization en Route for Enhanced CO2 Adsorption Properties[J]. Chem Commun,2014,50:1937-1940.
[13]	Chen Q,Liu D,Zhu J,et al. Mesoporous Conjugated Polycarbazole with High Porosity via Structure Tuning[J]. Macromolecules,2014,47(17):5926-5931.
[14]	Zhu Y,Zhang W.Reversible Tuning of Pore Size and CO2 Adsorption in Azobenzene Functionalized Porous Organic Polymers[J]. Chem Sci,2014,5(12):4957-4961.
[15]	Xiang Z,Mercado R,Huck J M,et al. Systematic Tuning and Multifunctionalization of Covalent Organic Polymers for Enhanced Carbon Capture[J]. J Am Chem Soc,2015,137(41):13301-13307.
[16]	Ogoshi T,Yamagishi T,Nakamoto Y.Pillar-Shaped Macrocyclic Hosts Pillar[n]arenes:New Key Players for Supramolecular Chemistry[J]. Chem Rev,2016,116(14):7937-8002.
[17]	Tan L,Li H,Tao Y,et al. Pillar[5]arene-Based Supramolecular Organic Frameworks for Highly Selective CO2 -Capture at Ambient Conditions[J]. Adv Mater,2014,26(41):7027-7031.
[18]	Dai D,Li Z,Yang J,et al. Supramolecular Assembly-Induced Emission Enhancement for Efficient Mercury(Ⅱ) Detection and Removal[J]. J Am Chem Soc,2019,141(11):4756-4763.
[19]	Wu M,Yang Y.A Fluorescent Pillarene Coordination Polymer[J]. Polym Chem,2019,10(23):2980-2985.
[20]	Li Z,Li X,Yang Y.Conjugated Macrocycle Polymer Nanoparticles with Alternating Pillarenes and Porphyrins as Struts and Cyclic Nodes[J]. Small,2019,15(12):1805509.
[21]	Ma Y,Chen L,Li C,et al. A fishing Rod-like Conjugated Polymer Bearing Pillar[5]arenes[J]. Chem Commun,2016,52:6662-6664.
[22]	Li X,Li Z,Yang Y.Tetraphenylethylene-Interweaving Conjugated Macrocycle Polymer Materials as Two-Photon Fluorescence Sensors for Metal Ions and Organic Molecules[J]. Adv Mater,2018,30(20):1800177.
[23]	Lin Q,Fan Y,Mao P,et al. Pillar[5]arene-Based Supramolecular Organic Framework with Multi-guest Detection and Recyclable Separation Properties[J]. Chem Eur J,2018,24(4):777-783.
[24]	Shi B,Guan H,Shangguan L,et al. A Pillar[5]arene-Based 3D Network Polymer for Rapid Removal of Organic Micropollutants from Water[J]. J Mater Chem A,2017,5(46):24217-24222.
[25]	Lan S,Zhan S,Ding J,et al. Pillar[n]arene-Based Porous Polymers for Rapid Pollutant Removal from Water[J]. J Mater Chem A,2017,5(6):2514-2518.
[26]	Ogoshi T,Yamafuji D,Tomohiro A,et al. Achiral Guest-Induced Chiroptical Changes of a Planar-Chiral Pillar[5]arene Containing One π-Conjugated Unit[J]. Chem Commun,2013,49:8782-8784.
[27]	Strutt N L,Fairen-Jimenez D,Iehl J,et al. Incorporation of an A1/A2-Difunctionalized Pillar[5]arene into a Metal-Organic Framework[J]. J Am Chem Soc,2012,134(42):17436-17439.
[28]	Ogoshi T,Shimada Y,Akutsu T,et al. A Rod-Like Phenolic π-Conjugated Polymer with Pillar[5]arene Units in Its Main Chain[J]. Polymer,2017,128:325-329.
[29]	Zhang C,Zhu P,Tan L,et al. Triptycene-Based Hyper-Cross-Linked Polymer Sponge for Gas Storage and Water Treatment[J]. Macromolecules,2015,48(23):8509-8514.
[30]	Kuhn P,Kr ger K,Thomas A,et al. “Everything Is Surface”:Tunable Polymer Organic Frameworks with Utrahigh Dye Sorption Capacity[J]. Chem Commun,2008,44:5815-5817.