5-丁氧基亚甲基-2-降冰片烯的合成及其加成聚合反应

贺晓慧,何福平,聂华荣,陈义旺*,王凯悌   

  1. (南昌大学高分子研究所，化学系 南昌 330031)
  • 收稿日期:2010-02-18 修回日期:2010-04-07 出版日期:2011-01-10 发布日期:2011-01-10
  • 通讯作者: 陈义旺，教授; Tel:0791-3969561; E-mail:ywchen@ncu.edu.cn; 研究方向：功能高分子的合成和应用
  • 基金资助:
    国家自然科学基金(50663002)江西省自然科学基金(2007GZC1727,2007GZH1704)资助项目

Synthesis and Addition Polymerization of 5-Butoxymethylenyl-2-norbornene

HE Xiao-Hui, HE Fu-Ping, NIE Hua-Rong, CHEN Yi-Wang*, WANG Kai-Ti   

  1. (Institute of Polymers,Department of Chemistry,Nanchang University,Nanchang 330031)
  • Received:2010-02-18 Revised:2010-04-07 Published:2011-01-10 Online:2011-01-10
  • Contact: Chen

PDF

1727

被引次数

3

摘要：

采用降冰片烯-5-甲醇和溴丁烷在氢化钠作用下合成了5-丁氧基亚甲基-2-降冰片烯，双-(β-酮萘胺)镍(Ⅱ)/B(C6F5)3催化体系使之聚合。 考察了聚合时间对其均聚合的影响以及5-丁氧基亚甲基-2-降冰片烯和降冰片烯不同摩尔投料比对其共聚行为的影响。 采用1H NMR、FTIR和TGA测试技术对所得的聚合物进行了结构表征和性能测试。 结果表明，双-(β-酮萘胺)镍(Ⅱ)/B(C6F5)3催化体系对5-丁氧基亚甲基-2-降冰片烯均聚和共聚具有较高的催化活性。 得到的均聚物和共聚物为加成型聚合物，料液中5-丁氧基亚甲基-2-降冰片烯的摩尔分数为10%~90%时，其在共聚物中的插入率为22.1%~76.9%，所得聚合物具有较好的热稳定性（Td＞360 ℃），在THF和CHCl3等许多普通溶剂中有很好的溶解性能。

关键词: 加成聚合, 丁氧基亚甲基降冰片烯, 聚降冰片烯, 镍催化剂

Abstract:

5-Butoxymethylenyl-2-norbornene(NBE-CH2OC4H9) was synthesized. Polynorbornenes with functional groups were obtained by homo and copolymerizations of norbornene derivatives catalyzed by bis(β-ketonaphthylamino)Ni(Ⅱ)/B(C6F5)3 system. Influences on polymerizations by changing polymerization time and copolymerization monomer feed ratios was examined. The catalytic bis(β-ketonaphthylamino)Ni(Ⅱ)/B(C6F5)3 system exhibited higher catalysis activity. The obtained polymers were characterized by 1H NMR, FTIR and TGA. Results indicated that the incorporation rate could reach 22.1%~76.9% ether units at a molar fraction of 10%~90% of the NBE-CH2OC4H9 in the monomer feed ratios; the polymerizations are confirmed to be vinyl-addition mode. The polymer has a good thermal stability(Td＞360 ℃) and is soluble in many common solvents, such as THF and CHCl3.