摘要/Abstract

摘要： 为减少析氧电位、提高电极的稳定性、降低能耗和成本,人们一直在努力合成各种过渡金属复合氧化物作为析氧的电催化材料^[1].研究表明,尖晶石型化合物NiCo₂O₄对氧的析出有较高的催化活性^[2].但因其制备方法多为喷涂热解法,需400℃以上温度,因此易发生相变而分解为一种富含Co的化合物^[3],很难得到所期望的电极催化活性.

关键词: 尖晶石型化合物NiCo₂O₄, 复合镀, 析氧电极

Abstract: The Ni-NiCo₂O₄ composite electrodes for oxygen evolution were prepared by composite electroplating technique. In the course of plating the particles of spinel NiCo₂O₄/(ca.4 μm) were easily codeposited on the nickel deposited electrode forming a high rough Ni-NiCo₂O₄ composite plating layer. The Ni-NiCo₂O₄ composite electrodes exhibited low oxygen overvoltage and good stability and had two Tafel slopes smaller than that of pure Ni plating electrode.

Key words: spinel NiCo₂O₄, composite electroplating, oxygen evolution electrode

蔡乃才, 张克立, 袁继兵, 刘勇, 孙聚堂. 用尖晶石型化合物NiCo₂O₄和复合镀技术制备析氧电极[J]. 应用化学, 1998, 0(6): 74-76.

Cai Naicai, Zhang Keli, Yuan Jibing, Liu Yong, Sun Jutang. Preparation of Oxygen Evolution Electrode from Spinel NiCo₂O₄ by Composite-Plating Technique[J]. Chinese Journal of Applied Chemistry, 1998, 0(6): 74-76.

[1]	廖登辉, 陈阵, 郭忠诚, 陆丽芳. 新型不锈钢基二氧化铅-碳化钨复合电极材料的研制[J]. 应用化学, 2013, 30(02): 196-202.
[2]	姜妍妍, 曹梅, 郭忠诚,陈步明. Ti阳极上电沉积制备Pb-聚丙烯腈-碳化钨复合镀层及其电化学性能[J]. 应用化学, 2011, 28(03): 308-313.
[3]	马洁, 刘辉, 石英, 贺晶, 姚忠科. 不同形状TiO2纳米材料在耐NaCl溶液及微生物腐蚀中的应用[J]. 应用化学, 2008, 25(7): 815-819.
[4]	石淑云, 马文英, 常立民, 陈丹, 王丽梅. 电沉积方式对Ni-nanoAl2O3复合镀层组织结构和耐蚀性能的影响[J]. 应用化学, 2008, 25(12): 1499-1501.
[5]	黄新民, 张胡海, 刘岩, 何美清, 吴玉程. 化学复合镀Ni-P-TiO2纳米颗粒涂层功能特性[J]. 应用化学, 2006, 23(3): 264-267.
[6]	姚素薇, 廖川平, 郭鹤桐. 锌电沉积与丙烯酸盐聚合的复合过程[J]. 应用化学, 1997, 0(2): 118-118.
[7]	王为, 郭鹤桐, 高建平, 覃奇贤. 复合镀层中ZrO₂微粒对基质Ni晶体结构的影响[J]. 应用化学, 1997, 0(1): 6-10.
[8]	程鹏里, 石秋芝, 张建民, 杨长春. 镍钴复合氧化物的制备和析氧活性[J]. 应用化学, 1994, 0(3): 32-35.

用尖晶石型化合物NiCo₂O₄和复合镀技术制备析氧电极

Preparation of Oxygen Evolution Electrode from Spinel NiCo₂O₄ by Composite-Plating Technique

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 8

编辑推荐

Metrics

本文评价