聚环氧乙烷环氧丙烷-盐复合物的结构和导电性

摘要/Abstract

摘要： 制备了室温电导率较高(10^-4S•cm^-1),力学性能较好的环氧乙烷和环氧丙烷共聚物-Li-ClO₄复合物薄膜,研究了共聚物组成对结晶及对复合物室温电导率的影响,考察了高氯酸锂浓度对复合物室温电导率的影响以及复合物电导的温度依赖关系,发现复合物中没有结晶配合物,其结晶度随聚合物结构和盐含量不同而变化,室温下呈弹性体。

关键词: 环氧乙烷环氧丙烷共聚物, 高氯酸锂, 高分子固体电解质, 聚集态结构

Abstract: The title copolymer was prepared and characterized by ¹HNMR, DSC, and mechanical property measurements. The sample appeared to be an elastomer at room temperature. The effects of the EO/PO ratio and LiClO₄ content of the copolymer-LiClO₄ complex on the crystallinity and conductivity have been studied. The conductivity of the LiClO₄ dopped copolymer film was 1.2?10^-4S/cm at room temperature obtained from AC impedance.

Key words: ethylene oxide-propylene oxide copolymer, lithium perchlorate, polymer solid electrolyte, aggregate state structure

齐力, 宋永贤, 董巍, 彭新生. 聚环氧乙烷环氧丙烷-盐复合物的结构和导电性[J]. 应用化学, 1993, 0(5): 61-65.

Qi Li, Song Yongxian, Dong Wei, Peng Xinsheng. STRUCTURE AND IONIC CONDUCTIVITY OF ETHYLENE OXIDE-PROPYLENE OXIDE COPOLYMER-LiClO₄ COMPLEX[J]. Chinese Journal of Applied Chemistry, 1993, 0(5): 61-65.

[1]	陈永春, 陈超, 曹红燕, 徐祖顺, 程时远. 聚甲基丙烯酸甲酯接枝聚氧乙烯在甲苯中的聚集态结构[J]. 应用化学, 2002, 19(7): 662-666.
[2]	崔敏慧, 吴正华, 邱思畴, 谢洪泉. 聚氧乙烯－高氯酸锂配合物电致变色光窗的研究[J]. 应用化学, 1996, 0(6): 39-41.
[3]	齐力, 林云青, 陈东霖. 环氧乙烷和环氧丙烷共聚物及其盐复合物的结晶与熔融[J]. 应用化学, 1995, 0(3): 97-99.
[4]	齐力, 宋永贤, 彭新生, 陈东霖. 环氧乙烷和环氧丙烷共聚物及其LiClO₄复合物的热性能[J]. 应用化学, 1994, 0(2): 116-118.
[5]	张利华, 于力, 张宏放, 綦玉臣, 莫志深, 陈东霖. 结晶聚合物的辐射效应 Ⅰ.γ-辐照尼龙1010的聚集态结构[J]. 应用化学, 1992, 0(5): 21-24.
[6]	熊静, 张玉喜, 赵晓江, 王佛松. 二甲氧基聚乙二醇增塑的P(EO-PO-AGE)-LiClO₄聚合物膜的离子电导[J]. 应用化学, 1990, 0(6): 14-18.
[7]	张宏放, 莫志深, 彭新生, 王佛松. 环氧树脂/聚氧化乙烯共混物及其与硫氰化钠络合物的结构研究(Ⅰ)[J]. 应用化学, 1989, 0(3): 31-36.
[8]	彭新生, 陈东霖, 王佛松. 高分子固体电解质研究的进展[J]. 应用化学, 1989, 0(1): 1-8.
[9]	谢东, 谢洪泉. 高分子固体电解质-聚醚-硫氰酸盐络合物的电导与结构关系[J]. 应用化学, 1989, 0(1): 46-49.