Sr3Cu5O8+x和CaSrCu5O5+x的结构和电学性质

摘要/Abstract

摘要： 继Y-Ba-Cu-O之后,具有更高T₅的Bi-Sr-Ca-Cu-O(简称BSCCO)体系的发现^[1,2]引起了人们对高温超导研究的兴趣。研究表明,在BSCCO中存在110K和80K2个超导相^[3,4]。由于在制备BSCCO过程中存在复杂的Ca、Sr和Cu复合氧化物,要得到稳定的110K相相当困难, 因此研究Ca-Sr-Cu-O系中间产物的生成条件、性质及其对超导材料的影响很有必要。

关键词: Sr₃Cu₅O_8+x, CaSrCu₅O_5+x结构, 电学性质

Abstract: The compounds with the compositions of Sr₃Cu₅O_8+x and CaSrCu₃O_5+x have been syn-thesized by solid phase reaction method. The crystal structures of both compounds are or-thorhombic with a = 3.950Å, b = 11.479Å and c = 13.420Å for Sr₃Cu₅O_8+x and a = 6.489Å,b = 11.280 Å and c = 12.240Å for CaSrCu₃O_5+x, respectively. The oxygen content and oxida-ation state of copper ion were analysized by the iodometric titration. The electric propertymeasurement indicates that both compounds are p-type semiconductor and have lower resistivity. They decomposes at around 936℃.

Key words: Sr₃Cu₅O_8+x, CaSrCu₅O_5+x, structure, electric property

孟建, 曾左韬, 任玉芳. Sr₃Cu₅O_8+x和CaSrCu₅O_5+x的结构和电学性质[J]. 应用化学, 1990, 0(4): 86-89.

Meng Jian, Zeng Zuotao, Ren Yufang. THE STRUCTRUE AND ELECTRIC PROPERTY OF Sr₃Cu₅O_8+x AND CaSrCu₃O_5+x[J]. Chinese Journal of Applied Chemistry, 1990, 0(4): 86-89.

[1]	史发年, 任玉芳, 孟建. Ln₂Mo₃O₉的制备、结构及电磁性质[J]. 应用化学, 1995, 0(2): 95-97.
[2]	李思温, 任玉芳. NdSr_1－χM_χNiO₄(M＝Ca,Ba)的合成,结构和电学磁学性[J]. 应用化学, 1994, 0(4): 50-53.
[3]	李思温, 任玉芳, 王鸿燕. Pr_2－xSr_xNiO_4±δ的合成、结构和电磁性质[J]. 应用化学, 1994, 0(3): 40-44.
[4]	张源魁, 任玉芳. La_1-xM_xFe_yCo_1-yO₃型复合氧化物(M=Sr,Ba)的合成、结构及电性能[J]. 应用化学, 1993, 0(6): 99-101.
[5]	任玉芳, 孟建. 磷化镝与磷化镱的光学性质和电学性质[J]. 应用化学, 1988, 0(3): 39-42.

Sr₃Cu₅O_8+x和CaSrCu₅O_5+x的结构和电学性质

THE STRUCTRUE AND ELECTRIC PROPERTY OF Sr₃Cu₅O_8+x AND CaSrCu₃O_5+x

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 5

编辑推荐

Metrics

本文评价