应用化学 ›› 1985, Vol. 0 ›› Issue (2): 33-38.
• 研究论文 • 上一篇 下一篇
章哲彦1, 曲淑华2, 张宏放2
收稿日期:
修回日期:
出版日期:
发布日期:
Zhang Zheyan1, Qu Shuhua2, Zhang Hongfang 2
Received:
Revised:
Published:
Online:
摘要： 研究了红外3100～2800cm-1谱区的聚丁二烯图谱,它是聚丁二烯的顺-1,4,反-1,4和1,2微观结构信息叠加谱区。用因素分析技术对聚丁二烯的微观结构进行了定量分析,与传统的分析方法和其它谱区的因素分析进行比较,结果显示3100～2800cm-1港区的因素分析为现用方法中最佳。
Abstract: The infrared spectra of polybutadiene in the region from 3100 to 2800 cm-1 have been investigated.The spectra give reliable information related to the microstructure of polybutadiene, i.e cis-1, 4 trans-1,4 and1,2. The microstructure of polybutadiene samples has been determined by factor analysis of IR spectra in the region from 3100 to 2800 cm-1 as well as from 1000 to 650 cm-1. The scectra from the first region were proved more reasonable for the microstructure determination in comparison with those usedin the traditional IR analysis.
章哲彦, 曲淑华, 张宏放. 以红外3100～2800cm-1谱分析聚丁二烯[J]. 应用化学, 1985, 0(2): 33-38.
Zhang Zheyan, Qu Shuhua, Zhang Hongfang . INFRARED ANALYSIS OF POLYBUTADIENE BY USING THE REGION FROM 3100cm-1 to 2800cm-1[J]. Chinese Journal of Applied Chemistry, 1985, 0(2): 33-38.