聚丁二烯有序多孔膜在热缩型聚乙烯膜上的收缩

doi:10.3724/SP.J.1095.2010.90217

摘要/Abstract

摘要：

采用溶剂散逸自组装制备了聚丁二烯（ＰＢ）有序多孔膜。水珠能在冷的高分子溶液表面凝结形成有序的阵列，溶剂蒸发后，高分子材料按照水珠排列的形貌形成了有序多孔膜。两性共聚物的加入能够起到稳定水滴的作用，从而确保多孔膜成为有序的结构。利用聚乙烯可收缩膜将聚丁二烯多孔膜收缩２次，得到长方形、梭形、条形和哑铃形的孔。孔的尺寸从微米级收缩至亚微米级，并对产生各种形状的机理进行了研究。

关键词: 热缩膜, 有序多孔膜, 溶剂散逸自组装

Abstract:

Microporous polymer honeycomb films with hexagonal pores were prepared by self-organization under humid conditions. The amphiphilic polymer acted as a stabilizer of condensed water droplets and prevented water droplets from fusion. The honeycomb film was shrunk by a shrinkable film. Various shapes could be formed upon the mechanical shrink deformation of hexagonal micro polymer meshes. Shapes such as rectangle, shuttle, slot and dumbbell were found in the shrunk honeycomb films. The pore size of honeycomb structure film (4~8 μm) was also shrunk to 130 nm. The deformation mechanism of the film was discussed.

Key words: thermal contracted film, regular porous film, solvent evaporation self organize

中图分类号:

0647

林松竹,贾若琨,杨莹,秦玉华,罗娟. 聚丁二烯有序多孔膜在热缩型聚乙烯膜上的收缩[J]. 应用化学, 2010, 27(03): 272-275.

LIN Song-Zhu*, JIA Ruo-Kun, YANG Ying, QIN Yu-Hua, LUO Juan. Shrinking of the Self-Organized Polybutadiene Microporous film Deposited on a Stretched Polymer film by Thermal Contraction[J]. Chinese Journal of Applied Chemistry, 2010, 27(03): 272-275.

参考文献

1. L Cui; Y Xuan, X Li; Y Ding; B Y Li; Y C Han, Langmuir, 21, 11696-11703.

2. M. Haupt; S. Miller; R. Suer; K. Thonke; A. Mourran; M. Moeller, Journal of Applied Physics, 2004, 96, 3065-3069.

3. T Nishikawa; M Nonomura; K Arai; J Hayashi; T Sawadaishi; Y Nishiura; M Hara; M Shimomura, Langmuir, 2003, 19, 6193-6201.

4. A Tsuruma; M Tanaka; N Fukushima M Shimomura, e-Journal of Surface Science and Nanotechnology, 2005, 3, 159-164.

5. M Tanaka; M Takebayashi; M Miyama; J Nishida; M Shimomura, Bio-Medical Materials and Engineering, 2004, 14, 439-446.

6. B Erdogan; L Song; J N. Wilson; J O. Park; M Srinivasarao; U H. F. Bunz, J.AM. CHEM. SOC. 2004, 126, 3678-3679.

7. G Widawski; Ml Rawiso; B Francols, Nature, 1994, 369, 387-389.

8. S I. Matsushia; N Kurono; T Sawadaishi; M Shimomura, Synthetic metals, 2004, 147, 237-240.

9. J Nishida; K Nishikawa; S-I Nishimura; S Wada; T Karino; T Nishikawa; K Ijiro; M Shimomura, Polymer Journal, 2002, 34, 166-174.

10. M S Park; J K Kim, Langmuir, 2004, 20, 5347-5352.

11. N. Maruyama; T. Koito; J. anishida; T. Sawadaishi; X. Cieren; K. Ijiro; O. Karthaus; M. Shimoumura, Thin Solid Films, 1998, 327-329, 854-856.

12. T Hayakawa; H Yokoyama, Langmuir, 2005, 21, 10288-10291.

13. E. Bormashenko; R. Pogreb; O. Stanevsky; Y. Bormashenko; O. Gendelman, Materials Letters, 2005, 59, 3553-3557.

14. Pitois; B. Francois, The European Physical Journal B, 1999, 8, 225-231.

15. H Yabu; M Shimomura, Langmuir, 2005, 21, 1709-1711.

16. O Karthaus; N Maruyama; X Cieren; M Shimomura; H Hasegawa; T Hashimoto, Langmuir, 2000, 16, 6071-6076.

17. B Zhao; C Li; Y Lu; X Wang; Z Liu; J Zhang, Polymer, 2005, 46, 9508-9513.

18. M S Park; J K Kin, Langmuir, 2005, 21, 11404-11408.

19. H Yabu; M Shimomura, Chem. Mater. 2005, 17, 5231-5234.

20. H Yabu; M Takebayashi; M Tanaka; M Shimomura, Langmuir, 2005, 21, 3235-3237.

21. H Yabu; R Jia; Y Matsuo; K Ijiro; S Yamamoto; F Nishino; T Takaki; M Kuwahara; M Shimomura, Advanced Materials, 2008, 20, 1-5

[1]	贾若琨, 李婷婷, 周诗宇. 聚苯乙烯-嵌段-聚丁二烯有序多孔膜在可收缩膜上的形变研究和光学性质[J]. 应用化学, 2014, 31(05): 560-565.
[2]	贾若琨, 杨莹, 罗娟, 甄丽颖. 溶剂散逸自组装制备超疏水针垫阵列膜[J]. 应用化学, 2010, 27(09): 1046-1049.
[3]	贾若琨, 闫永楠, 李翠霞, 杨珊, 白玉白. 溶剂散逸自组装制备高分子有序微透镜阵列[J]. 应用化学, 2009, 26(5): 566-570.