原位生长的α-Fe2O3/ZnO异质纳米棒阵列对乙醇气体的高选择性检测

摘要/Abstract

摘要： 采用两步溶液法在陶瓷管上原位生长了ZnO纳米棒阵列,然后以ZnO纳米棒为载体,通过水热法在其表面负载α-Fe₂O₃纳米粒子,生成异质α-Fe₂O₃/ZnO复合纳米材料。 α-Fe₂O₃/ZnO纳米棒直径30~80 nm,长1 μm左右,交叉排列形成纳米棒阵列,α-Fe₂O₃纳米粒子粒径约10 nm,均匀分布在ZnO纳米棒表面。将纯ZnO和α-Fe₂O₃/ZnO纳米棒阵列制成气敏元件,测试并对比了2种气敏元件的气敏性能,揭示其气敏机理。结果表明:α-Fe₂O₃纳米粒子的复合显著提高了ZnO纳米棒阵列对乙醇气体的灵敏度和选择性,在工作温度370 ℃时,对100 μL/L乙醇气体的响应值为85.4,是同条件下ZnO器件对乙醇响应值(9.4)的9.1倍,响应时间7 s,最低检出限为0.01 μL/L。相关研究可以应用于痕量乙醇的快速、高灵敏度和高选择性检测。

关键词: 原位生长法, α-Fe₂O₃, ZnO, 纳米棒阵列, 异质结构

Abstract: ZnO nanorod arrays were grown in situ on ceramic tubes by a two-step solution method. Then α-Fe₂O₃ nanoparticles were loaded on the surface of ZnO nanorods via a hydrothermal method to obtain heterogeneous α-Fe₂O₃/ZnO composites. The α-Fe₂O₃/ZnO nanorods are about 30~80 nm in diameter and 1 μm in length, which are cross-arranged to form nanorod arrays. α-Fe₂O₃ nanoparticles with a diameter of about 10 nm distributed on the surface of ZnO nanorods evenly. The gas-sensing properties of the sensors based on pristine ZnO and α-Fe₂O₃/ZnO nanorod arrays were compared, and the gas-sensing mechanism was revealed. The results show that the decoration of α-Fe₂O₃ nanoparticles significantly enhances the sensitivity and selectivity of ZnO nanorod arrays sensors to ethanol at the working temperature of 370 ℃. The response of α-Fe₂O₃/ZnO sensor to 100 μL/L of ethanol is 85.4, which is 9.1 times higher than that of pure ZnO sensor (9.4) determined under the same conditions. The response time is 7 s, and the detection limit is 0.01 μL/L. The work can be applied to the rapid, high sensitivity and selectivity detection for trace ethanol.

Key words: In situ growth, α-Fe₂O₃, ZnO, Nanorod arrays, Heterostructure

中图分类号:

O614.8

隋丽丽, 黄微微, 王平, 徐英明, 程晓丽, 霍丽华, 姜惠烨, 赵冰, 张文治, 王政军, 刘亚红. 原位生长的α-Fe₂O₃/ZnO异质纳米棒阵列对乙醇气体的高选择性检测[J]. 应用化学, 2021, 38(7): 0-0.

SUI Li-Li, HUANG Wei-Wei, WANG Ping, XU Ying-Ming, CHENG Xiao-Li, HUO Li-Hua, JIANG Hui-Ye, ZHAO Bing, ZHANG Wen-Zhi, WANG Zheng-Jun, LIU Ya-Hong. In Situ Deposited Heterogeneous α-Fe₂O₃/ZnO Nanorod Arrays for Highly Selective Detection of Ethanol[J]. Chinese Journal of Applied Chemistry, 2021, 38(7): 0-0.

参考文献

[1] CAO J, ZHANG N R, WANG S M, et al. Researching the crystal phase effect on gas sensing performance in In₂O₃ nanofibers[J]. Sens Actuators B: Chem, 2020, 305: 127475.
[2] DU H Y, YANG W, YI W C, et al. Oxygen-plasma-assisted enhanced acetone-sensing properties of ZnO nanofibers by electrospinning[J]. ACS Appl Mater Interfaces, 2020, 12(20): 23084-23093.
[3] ZHAO D, ZHANG X F, SUI L L, et al. C-doped TiO₂ nanoparticles to detect alcohols with different carbon chains and their sensing mechanism analysis[J]. Sens Actuators B: Chem, 2020, 312: 127942.
[4] TIAN K, WANG X X, YU Z Y, et al. Hierarchical and hollow Fe₂O₃ nanoboxes derived from metal-organic frameworks with excellent sensitivity to H₂S[J]. ACS Appl Mater Interfaces, 2017, 9(35): 29669-29676.
[5] XU S, XU Y, ZHAO H, et al. Sensitive gas-sensing by creating adsorption active sites: coating an SnO₂ layer on triangle arrays[J]. ACS Appl Mater Interfaces, 2018, 10(34): 29092-29099.
[6] SUI L L, ZHANG X F, CHENG X L, et al. Au-loaded hierarchical MoO₃ hollow spheres with enhanced gas sensing performance for the detection of BTX (benzene, toluene, and xylene) and the sensing mechanism[J]. ACS Appl Mater Interfaces, 2017, 9(2): 1661-1670.
[7] 梁继然, 张叶, 杨然, 等. VO₂(B)/ZnO异质复合纳米棒结构的室温NH₃敏感性能研究[J]. 无机材料学报, 2018, 33(12): 1323-1329.
LIANG J R, ZHANG Y, YANG R, et al. Room-temperature NH₃ gas sensing property of VO₂(B)/ZnO hierarchical heterogeneous composite with nanorod structure[J]. J Inorg Mater, 2018, 33(12): 1323-1329.
[8] AZIZ A, TIWALE N, HODGE S A, et al. Core-shell electrospun polycrystalline ZnO nanofibers for ultrasensitive NO₂ gas sensing[J]. ACS Appl Mater Interfaces, 2018, 10(50): 43817-43823.
[9] 杜海英, 姚朋军, 王兢, 等. 异质复合结构纳米纤维SnO₂/ZnO的制备及其气敏特性研究[J]. 无机材料学报, 2018, 33(4): 453-461.
DU H Y, YAO P J, WANG J, et al. Preparation and gas sensing property of SnO₂/ZnO composite hetero-nanofibers using two-step method[J]. J Inorg Mater, 2018, 33(4): 453-461.
[10] PAN Z Z, SUN F Q, ZHU X M, et al. Electrodeposition-based in situ construction of a ZnO-ordered macroporous film gas sensor with enhanced sensitivity[J]. J Mater Chem A, 2019, 7(3): 1287-1299.
[11] SUI L L, YU T T, ZHAO D, et al. In situ deposited hierarchical CuO/NiO nanowall arrays film sensor with enhanced gas sensing performance to H₂S[J]. J Hazard Mater, 2020, 385: 121570.
[12] YANG H Y, CHENG X L, ZHANG X F, et al. A novel sensor for fast detection of triethylamine based on rutile TiO₂ nanorod arrays[J]. Sens Actuators B: Chem, 2014, 205: 322-328.
[13] YU T T, CHENG X L, ZHANG X F, et al. Highly sensitive H₂S detection sensors at low temperature based on hierarchically structured NiO porous nanowall arrays[J]. J Mater Chem A, 2015, 3(22): 11991-11999.
[14] LI Z J, WANG N N,LIN Z J, et al. Room-temperature high-performance H₂S sensor based on porous CuO nanosheets prepared by hydrothermal method[J]. ACS Appl Mater Interfaces, 2016, 8(32): 20962-20968.
[15] WANG P, ZHENG Z K, CHENG X L, et al. Ionic liquid-assisted synthesis of α-Fe₂O₃ mesoporous nanorod arrays and their excellent trimethylamine gas-sensing properties for monitoring fish freshness[J]. J Mater Chem A, 2017, 5(37): 19846-19856.
[16] HUANG L M, FAN H Q. Room-temperature solid state synthesis of ZnO/α-Fe₂O₃ hierarchical nanostructures and their enhanced gas-sensing properties[J]. Sens Actuators B: Chem, 2012, 171/172: 1257-1263.
[17] SONG X P, LI L, CHEN X, et al. Enhanced triethylamine sensing performance of α-Fe₂O₃ nanoparticle/ZnO nanorod heterostructures[J]. Sens Actuators B: Chem, 2019, 298: 126917.
[18] ZHANG B W, FU W Y, MENG X W, et al. Synthesis and enhanced gas sensing properties of flower-like ZnO/α-Fe₂O₃ core-shell nanorods[J]. Ceram Int, 2017, 43(8): 5934-5940.
[19] LI Y G, QIAO L,YAN D, et al. Preparation of Au-sensitized 3D hollow SnO₂ microspheres with an enhanced sensing performance[J]. J Alloys Compd, 2014, 586: 399-403.
[20] LIANG Y C, HUNG C S. Design of hydrothermally derived Fe₂O₃ rods with enhanced dual functionality via sputtering decoration of a thin ZnO coverage layer[J]. ACS Omega, 2020, 5(26): 16272-16283.
[21] CHEN Y, LI H, MA Q, et al. ZIF-8 derived hexagonal-like α-Fe₂O₃/ZnO/Au nanoplates with tunable surface heterostructures for superior ethanol gas-sensing performance[J]. Appl Surf Sci, 2018, 439: 649-659.
[22] ZHANG R, ZHANG T, ZHOU T T, et al. Fast and real-time acetone gas sensor using hybrid ZnFe₂O₄/ZnO hollow spheres[J]. RSC Adv, 2016, 6(71): 66738-66744.
[23] SUI L L, SONG X X, CHENG X L, et al. An ultraselective and ultrasensitive TEA sensor based on α-MoO₃ hierarchical nanostructures and the sensing mechanism[J]. CrystEngComm, 2015, 17(34): 6493-6503.
[24] ZHANG R, ZHOU T, WANG L, et al. The Synthesis and fast ethanol sensing properties of core-shell SnO₂@ZnO composite nanospheres using carbon spheres as templates[J]. New J Chem, 2016, 40: 6796-6802.
[25] ZHOU L K, ZENG W, LI Y. A facile one-step hydrothermal synthesis of a novel NiO/ZnO nanorod composite and its enhanced ethanol sensing property[J]. Mater Lett, 2019, 254: 92-95.
[26] HUI G Z, ZHU M Y, YANG X L, et al. Highly sensitive ethanol gas sensor based on CeO₂/ZnO binary heterojunction composite[J]. Mater Lett, 2020, 278: 128453.
[27] LI B, LIU J Y, LIU Q, et al. Core-shell structure of ZnO/Co₃O₄ composites derived from bimetallicorganic frameworks with superior sensing performance for ethanol gas[J]. Appl Surf Sci, 2019, 475: 700-709.
[28] ZHOU X, XIAO Y, WANG M, et al. Highly enhanced sensing properties for ZnO nanoparticle-decorated round-edged α-Fe₂O₃ hexahedrons[J]. ACS Appl Mater Interfaces, 2015, 7(16): 8743-8749.
[29] WANG Y, LIU C Y, WANG Z, et al. Sputtered SnO₂: NiO thin films on self-assembled Au nanoparticle arrays for mems compatible NO₂ gas sensors[J]. Sens Actuators B: Chem, 2019, 278: 28-38.
[30] MENG D, LIU D Y, WANG G S, et al. Low-temperature formaldehyde gas sensors based on NiO-SnO₂ heterojunction microflowers assembled by thin porous nanosheets[J]. Sens Actuators B: Chem, 2018, 273: 418-428.

原位生长的α-Fe₂O₃/ZnO异质纳米棒阵列对乙醇气体的高选择性检测

In Situ Deposited Heterogeneous α-Fe₂O₃/ZnO Nanorod Arrays for Highly Selective Detection of Ethanol

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	隋丽丽, 黄微微, 王平, 徐英明, 程晓丽, 霍丽华, 姜惠烨, 赵冰, 张文治, 王政军, 刘亚红. 原位生长的α-Fe₂O₃/ZnO异质纳米棒阵列对乙醇气体的高选择性检测[J]. 应用化学, 2021, 38(7): 857-865.
[2]	郝文文, 赵丹, 李延春, 楚文玲, 吕成伟, 石雷. 高分散纳米银催化剂一锅高效催化生物质基甘油和苯胺合成3-甲基吲哚[J]. 应用化学, 2019, 36(4): 465-473.
[3]	贾若琨, 赵光宇, 林松竹, 靳军灿. 共沸蒸馏法制备CuO-ZnO/Al₂O₃催化剂及其对催化性能的影响[J]. 应用化学, 2015, 32(5): 570-575.
[4]	赵海刚, 李彩虹, 王红强, 李茹, 张光辉. 焙烧温度对ZnO粉体结晶及光学性能的影响[J]. 应用化学, 2014, 31(02): 188-192.
[5]	王真真, 李方方, 郭涵, 冯九菊, 王爱军. 水热法原位合成纳米氧化锌阵列及其光催化应用[J]. 应用化学, 2013, 30(06): 667-672.
[6]	刘智勇, 徐文涛, 王宁, 杨小牛. 喷涂法制备大面积倒置聚合物光伏器件[J]. 应用化学, 2012, 29(12): 1423-1427.
[7]	许泳吉, 张利, 赵雪萍. 纳米片状ZnO的室温制备及其胶状前体的稳定性分析[J]. 应用化学, 2012, 29(09): 1036-1040.
[8]	周海燕, 彭银. 以CuC₂O₄微球为模板可控合成一维CuC₂O₄/ZnO异质结构[J]. 应用化学, 2012, 29(01): 52-56.
[9]	马隽, 朱娜. 担载Na对Cu-ZnO/SiO2催化剂结构及催化仲丁醇脱氢反应活性的影响[J]. 应用化学, 2011, 28(12): 1397-1401.
[10]	宫丽红, 叶彩, 安茂忠. 一维ZnO纳米棒阵列的水热合成[J]. 应用化学, 2011, 28(02): 164-167.
[11]	王炎英, 彭丽, 詹国庆. 氯化血红素在纳米氧化锌碳糊修饰电极上的电化学行为[J]. 应用化学, 2010, 27(10): 1204-1208.
[12]	梁英, 刘英. 水热合成掺Fe氧化锌复合材料及其光催化活性[J]. 应用化学, 2009, 26(10): 1247-1249.
[13]	过家好, 何晓英, 蔡生民, 郭敏, 陈秀英, 彭孝军. 新型菁类染料cy5敏化zno纳米晶电极[J]. 应用化学, 2007, 24(4): 383-387.
[14]	侯林瑞, 原长洲, 彭秧. bi38zno58光催化剂的制备及其光催化性能[J]. 应用化学, 2007, 24(2): 206-209.
[15]	侯林瑞, 原长洲, 彭秧. 磁载光催化剂ag-tio2/zno/γ-fe2o3的制备及其光催化性能[J]. 应用化学, 2006, 23(11): 1278-1281.