喷墨打印聚合物薄膜均匀性调控研究进展

doi:10.11944/j.issn.1000-0518.2018.02.170346

摘要/Abstract

摘要：

聚合物发光显示材料具有发光颜色在全可见光区可调、可溶液简单加工及适用于柔性大面积基底的特点,成为目前研究的热点。在聚合物发光薄膜图案化技术中,喷墨打印因为具有加工过程简单高效、适用于溶液方式加工、柔性的加工过程等特点而被认为是最具有应用潜力的技术。高质量聚合物薄膜的制备是高精度发光显示器件制作的关键,但喷墨打印液滴在干燥过程中通常伴随着“咖啡环”现象,造成薄膜不均匀沉积。因此,消除“咖啡环”现象,实现聚合物薄膜的均匀沉积,是喷墨打印高性能器件的重要研究方向。本文主要论述了“咖啡环”效应的产生机理,如何抑制喷墨打印聚合物薄膜加工过程中的“咖啡环”效应,最终实现聚合物薄膜均匀性调控。

关键词: 喷墨打印, 聚合物薄膜, 咖啡环效应

Abstract:

Flat panel displays(FPDs) of polymer light-emitting diodes(PLEDs) attract more attention in this field because of the color tunability of polymer materials within the entire visible spectrum, simple solution processability, and suitability for large area and flexible substrates. For the patterning method of polymer light-emitting films, inkjet printing is a potential technique for applications because of its simple and high efficient patterning process, suitability for solution process, flexibility of the patterning process, and easiness to integration and automatization. The deposition of high quality polymer film is essential for fabricating high-performance PLEDs. However, a ring-shaped film is often formed on the substrate due to the “coffee ring” effect in inkjet printing. Therefore, it is essential to eliminate the “coffee ring” effect to achieve uniform deposition of polymer film. In this paper, we review the progress on avoiding “coffee ring” effect to achieve high uniformity of inkjet printing polymer films.

Key words: inkjet printing, polymer film, coffee ring effect

林杨鸣,曲轶,于新红,韩艳春. 喷墨打印聚合物薄膜均匀性调控研究进展[J]. 应用化学, 2018, 35(2): 129-136.

LIN Yangming,QU Yi,YU Xinhong,HAN Yanchun. Research Progress on Modulation of Film Thickness Uniformity of Polymer Films by Inkjet Printing[J]. Chinese Journal of Applied Chemistry, 2018, 35(2): 129-136.

参考文献

[1]	Pardo D A,Jabbour G E,Peyghambarian N.Application of Screen Printing in the Fabrication of Organic Light-Emitting Devices[J]. Adv Mater,2000,12(17):1249-1252.
[2]	Granlund T,Nyberg T,Roman L S,et al.Patterning of Polymer Light-Emitting Diodes with Soft Lithography[J]. Adv Mater,2000,12(4):269-273.
[3]	Muller C D,Falcou A,Reckefuss N,et al.Multi-colour Organic Light-emitting Displays by Solution Processing[J]. Nature,2003,421(6925):829-833.
[4]	Blanchet G B,Loo Y L,Rogers J A,et al.Large Area, High Resolution, Dry Printing of Conducting Polymers for Organic Electronics[J]. Appl Phys Lett,2003,82(3):463-465.
[5]	Hebner T R,Wu C C,Marcy D,et al.Ink-jet Printing of Doped Polymers for Organic Light Emitting Devices[J]. Appl Phys Lett,1998,72(5):519-521.
[6]	Hebner T R,Sturm J C.Local Tuning of Organic Light-emitting Diode Color by Dye Droplet Application[J]. Appl Phys Lett,1998,73(13):1775-1777.
[7]	Chang S C,Bharathan J,Yang Y.Dual-color Polymer Light-emitting Pixels Processed by Hybrid Inkjet Printing[J]. Appl Phys Lett,1998,73(18):2561-2563.
[8]	Kawase T,Shimoda T,Sirringhaus H,et al.Inkjet Printing of Polymer Thin Film Transistors[J]. Thin Solid Films,2003,438:279-287.
[9]	Wang J Z,Gu J,Zenhausern F,et al.Low-cost Fabrication of Submicron All Polymer Field Effect Transistors[J]. Appl Phys Lett,2006,88(13):133502.
[10]	Marin V,Holder E,Wienk M M,et al.Ink-jet Printing of Electron Donor/Acceptor Blends:Towards Bulk Heterojunction Solar Cells[J]. Macromol Rapid Commun,2005,26(4):319-324.
[11]	Calvert P.Inkjet Printing for Materials and Devices[J]. Chem Mater,2001,13(10):3299-3305.
[12]	Danzebrink R,Aegerter M A.Deposition of Micropatterned Coating Using an Ink-jet Technique[J]. Thin Solid Films,1999,351(1-2):115-118.
[13]	Deegan R D,Bakajin O,Dupont T F,et al.Capillary Flow as the Cause of Ring Stains from Dried Liquid Drops[J]. Nature,1997,389(6653):827-829.
[14]	Deegan R D,Bakajin O,Dupont T F,et al.Contact Line Deposits in an Evaporating Drop[J]. Phys Rev E,2000,62(1):756-765.
[15]	Deegan R D.Pattern Formation in Drying Drops[J]. Phys Rev E,2000,61(1):475-485.
[16]	Sun J Z,Bao B,He M,et al.Recent Advances in Controlling the Depositing Morphologies of Inkjet Droplets[J]. ACS Appl Mater Interfaces,2015,7(51):28086-28099.
[17]	Anyfantakis M,Baigl D.Manipulating the Coffee-Ring Effect:Interactions at Work[J]. Chem Phys Chem,2015,16(13):2726-2734.
[18]	Soltman D,Subramanian V.Inkjet-Printed Line Morphologies and Temperature Control of the Coffee Ring Effect[J]. Langmuir,2008,24(5):2224-2231.
[19]	van den Berg A M J,de Laat A W M,Smith P J,et al. Geometric Control of Inkjet Printed Features Using a Gelating Polymer[J]. J Mater Chem,2007,17(7): 677-683.
[20]	Wang L.Inkjet Printed Colloidal Photonic Crystal Microdot with Fast Response Induced by Hydrophobic Transition of Poly(N-isopropyl acrylamide)[J]. J Mater Chem,2012,22(40):21405-21411.
[21]	Xing R B,Ye T L,Ding Y,et al.Thickness Uniformity Adjustment of Inkjet Printed Light-emitting Polymer Films by Solvent Mixture[J]. Chinese J Chem,2013,31(11):1449-1454.
[22]	Yunker P J,Still T,Lohr M A,et al.Suppression of the Coffee-Ring Effect by Shape-Dependent Capillary Interactions[J]. Nature,2011,476(7360):308-311.
[23]	Bigioni T P,Lin X M,Nguyen T T,et al.Kinetically Driven Self Assembly of Highly Ordered Nanoparticle Monolayers[J]. Nat Mater,2006,5(4):265-270.
[24]	Still T,Yunker P J,Yodh A G.Surfactant-Induced Marangoni Eddies Alter the Coffee-Rings of Evaporating Colloidal Drops[J]. Langmuir,2012,28(11):4984-4988.
[25]	Tekin E,Holder E,Kozodaev D,et al.Controlled Pattern Formation of Poly[2-methoxy-5-(2'-ethylhexyloxyl)-1,4-phenylenevinylene](MEH-PPV) by Ink-Jet Printing[J]. Adv Funct Mater,2007,17(2):277-284.
[26]	Fischer B J.Particle Convection in an Evaporating Colloidal Droplet[J]. Langmuir,2002,18(1):60-67.
[27]	Hu H,Larson R G.Evaporation of a Sessile Droplet on a Substrate[J]. J Phys Chem B,2002,106(6):1334-1344.
[28]	Hu H,Larson R G.Analysis of the Microfluid Flow in an Evaporating Sessile Droplet[J]. Langmuir,2005,21(9):3963-3971.
[29]	Hu H,Larson R G.Marangoni Effect Reverses Coffee-ring Depositions[J]. J Phys Chem B,2006,110(14):7090-7094.
[30]	Hu H,Larson R G.Analysis of the Effects of Marangoni Stresses on the Microflow in an Evaporating Sessile Droplet[J]. Langmuir,2005,21(9):3972-3980.
[31]	Hendarto E,Gianchandani Y B.Size Sorting of Floating Spheres Based on Marangoni Forces in Evaporating Droplets[J]. J Micromech Microeng,2013,23(7):450-457.
[32]	Ristenpart W D,Kim P G,Domingues C,et al.Influence of Substrate Conductivity on Circulation Reversal in Evaporating Drops[J]. Phys Rev Lett,2007,99(23):234502.
[33]	Lim J A,Lee W H,Lee H S,et al.Self-Organization of Ink-jet-Printed Triisopropylsilylethynyl Pentacene via Evaporation-Induced Flows in a Drying Droplet[J]. Adv Funct Mater,2008,18(2):229-234.
[34]	de Gans B G,Schubert U S. Inkjet Printing of Well-defined Polymer Dots and Arrays[J]. Langmuir,2004,20(18):7789-7793.
[35]	Tekin E,de Gans B J,Schubert U S. Ink-jet Printing of Polymers From Single Dots to Thin Film Libraries[J]. J Mater Chem,2004,14(17):2627-2632.
[36]	Karabasheva S,Baluschev S,Gral K.Microstructures on Soluble Polymer Surfaces via Drop Deposition of Solvent Mixtures[J]. Appl Phys Lett,2006,89(3):231110.
[37]	Ko H Y,Park J,Shin H,et al.Rapid Self-Assembly of Monodisperse Colloidal Spheres in an Ink-Jet Printed Droplet[J]. Chem Mater,2004,16(22):4212-4215.
[38]	Kuang M X,Wang J X,Bao B,et al.Inkjet Printing Patterned Photonic Crystal Domes for Wide Viewing-Angle Displays by Controlling the Sliding Three Phase Contact Line[J]. Adv Opt Mater,2014,2(1):34-38.
[39]	Li Y F,Sheng Y J,Tsao H K.Evaporation Stains:Suppressing the Coffee-Ring Effect by Contact Angle Hysteresis[J]. Langmuir,2013,29(25):7802-7811.