纳米ZnS、CdS水热合成及其表征

摘要/Abstract

摘要： Ⅱ B-Ⅵ A族化合物是主要的半导体发光材料,广泛应用于各种发光与显示装置.可采用气相反应、固气相反应及液相反应等方法制备硫化锌和硫化锅.但产物晶粒不规则且分布很宽.而热分解硫代乙酸胺法严重团聚.本文以水热方法制备球状闪锌矿型硫化锌和球状β-硫化锡粉末.

关键词: 硫化锌, 硫化镉, 水热技术

Abstract: Hydrothermal treatment was successfully used to prepare pure nanocrystalline ZnS and CdS from respective amorphous sulfides. XRD indicated that both products were of cubic phase. The electron microscopy image showed that the average particle size of ZnS and CdS was about 7 nm and 5 nm respectively. The ZnS and CdS powders have narrow particle size distribution and ZnS possesses good IR transmittance in the range of 400 to 5000 cm^-1.

Key words: ZnS, CdS, hydrothermal treatment

苏宜, 谢毅, 陈乾旺, 钱逸泰. 纳米ZnS、CdS水热合成及其表征[J]. 应用化学, 1996, 0(5): 56-57.

Su Yi, Xie Yi, Chen Qianwang, Qian Yitai. Hydrothermal Preparation and Characterization of Nanocrystalline ZnS and CdS[J]. Chinese Journal of Applied Chemistry, 1996, 0(5): 56-57.

[1]	崔铁钰, 崔放, 李垚. 硫化镉/二氧化硅复合材料的合成[J]. 应用化学, 2013, 30(06): 730-732.
[2]	苏中华, 王亚静, 赵环, 胡娅梅, 唐春然, 李霞飞, 李进, 曾云龙. 以CdS量子点为荧光探针测定痕量铜[J]. 应用化学, 2011, 28(07): 842-848.
[3]	何铁石,任凤梅,张晶,周正发,徐卫兵. 溶液沉淀法制备ZnS-氟碳聚合物电纺纤维光催化复合材料[J]. 应用化学, 2009, 26(09): 1108-1110.
[4]	叶敏, 张友玉, 杨琴, 张雨琴, 谭平, 姚守拙. 半胱胺修饰的CdS纳米粒子荧光猝灭法测定锰离子[J]. 应用化学, 2008, 25(5): 534-538.
[5]	顾晓梅, 戴洁, 李淑华. zns与三乙烯四胺配合物的制备及光催化活性[J]. 应用化学, 2007, 24(1): 49-52.
[6]	王强, 赵军钗, 蒋世春, 姬相玲, 安立佳, 姜炳政. 模板法室温合成CdS纳米棒[J]. 应用化学, 2006, 23(1): 7-11.
[7]	张震雷, 吴庆生, 丁亚平. Cds纳米微粒的聚四氟乙烯多孔膜法制备及其表面修饰[J]. 应用化学, 2004, 21(8): 762-765.
[8]	李文戈, 朱琴玉, 戴洁, 蒋正静, 卞国庆. ZnS与1,3-丙二胺高聚配合物的制备及光催化活性[J]. 应用化学, 2002, 19(10): 928-931.
[9]	黄宵滨, 马季铭, 程虎民, 赵振国, 齐利民. 乳状液法制备ZnS纳米粒子[J]. 应用化学, 1997, 0(1): 117-118.
[10]	徐宝庆, 徐兆华, 包碧年, 孙炳方, 张华杰. 硫化锌镉基质荧光粉灼烧时的相变[J]. 应用化学, 1988, 0(2): 90-92.

纳米ZnS、CdS水热合成及其表征

Hydrothermal Preparation and Characterization of Nanocrystalline ZnS and CdS

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 10

编辑推荐

Metrics

本文评价