交联1,4－顺式聚丁二烯的取向结晶

摘要/Abstract

摘要： 用WAXD和SAXS研究交联1,4-顺式聚丁二烯的取向结晶。结果表明:该试样在拉伸状态时,形成折叠链片晶,而不是伸直链纤维晶。片晶之间不断产生新的片晶,使长周期减小,并且片晶的横向尺寸不断增大,由此导致结晶度增大。

Abstract: Oriented crystallization of cross linked cis-1,4-polybutadiene was investigated by WAXD and SAXS. The results showed that the samples formed "folded chain"lamellar crystallites rather than "extended chain" crystallites in the stretched state. Because new lamellar crystallites continuosly formed between old ones, the long period decreased and the lateral dimension increased gradually,thus resulting in the increase of crystallinity.

Key words: cis-polybutadiene, oriented crystallization, lamellar crystallite, draw ratio, long period

朱育平, 叶宇达. 交联1,4－顺式聚丁二烯的取向结晶[J]. 应用化学, 1996, 0(2): 26-28.

Zhu Yuping, Ye Yuda. Oriented Crystallization of Crosslinked Cis-1, 4- Polybutadiene[J]. Chinese Journal of Applied Chemistry, 1996, 0(2): 26-28.

[1]	苗中硕,门永锋. 快速扫描量热法研究聚对苯二甲酸-1,4-环己烷二甲醇酯的结晶和熔融行为[J]. 应用化学, 2020, 37(6): 642-649.
[2]	刘浩, 赵贝贝, 商少明, 顾丹. 煅烧工艺对熔盐法合成钛钾镁片晶的影响[J]. 应用化学, 2017, 34(10): 1195-1201.
[3]	李许可, 王俏, 姜志勇, 门永锋. 聚己内酯在α和β松弛过程中的微观结构演化[J]. 应用化学, 2012, 29(04): 388-391.
[4]	赵慧, 董为民, 张学全, 门永锋. 用DSC研究稀土顺式聚丁二烯的低温结晶与熔融行为[J]. 应用化学, 2008, 25(10): 1233-1236.
[5]	胡继文, 沈家瑞, 黄勇. 硬弹性聚丙烯的排状堆积片晶[J]. 应用化学, 2003, 20(5): 466-469.
[6]	莫志深, 杨宝泉, 薛小芙, 孟昭富, 王煜明. 尼龙-1010 SAXS研究[J]. 应用化学, 1991, 0(6): 33-36.
[7]	何永钜, 景遐斌, 王佛松. 高顺式聚丁二烯的低温红外光谱[J]. 应用化学, 1988, 0(6): 53-56.

交联1,4－顺式聚丁二烯的取向结晶

Oriented Crystallization of Crosslinked Cis-1, 4- Polybutadiene

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 7

编辑推荐

Metrics

本文评价