LDPE/EVA共混体系的结晶行为

于旻1, 杨连军1, 古利新2, 李三喜2   

  1. 1. 中国科学院长春应用化学研究所 130022 长春;
    2. 沈阳化工学院高分子材料系 沈阳
  • 收稿日期:1992-03-11 修回日期:1992-07-27 出版日期:1993-04-10 发布日期:1993-04-10

CRYSTLLIZATION BEHAVIOUR OF LDPE/EVA BLENDS

Yu Min1, Yang Lianjun1, Gu Lixin2, Li Sanxi2   

  1. 1. Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, 130022 Changchun;
    2. Polymer Science Department, Shenyang Institute of Technology, Shenyang
  • Received:1992-03-11 Revised:1992-07-27 Published:1993-04-10 Online:1993-04-10

PDF

581

被引次数

21

摘要： 本文通过DSC、WAXD、偏光显微镜、DMA等方法,对LDPE/EVA共混体系进行了研究。结果表明,EVA可使LDPE的熔融峰温提高15℃。并在LDPE结晶过程中起稀释剂作用。LDPE/EVA共混体系为非晶相相容。

关键词: LDPE, EVA, 共混物, 结晶行为

Abstract: The crystallization and dynamic mechanical behaviour of LDPE/EVA blends were studied by DSC, WAXD, optical microscopy. Results showed that the melting peak temperature of the LDPE in the LDPE/EVA blends was 15℃ higher than that of the pure LDPE. The EVA acts as a diluent in the crystallization of the LDPE. The LDPE/EVA blend system was compatible in amorphous regions.

Key words: LDPE, EVA, blend, crystallization