摘要： 前曾报道季戊四醇在461.60K有一个固-固相变,其相交含为41.37kJmol^-1^[1]。但是,作为低温储能材料,该物质的相变温度偏高。从有关固-固相变储能材料的热力学研究中,我们发现三甲醇丙烷-季戊四醇固体溶液具有较低的固-固相变温度。本文测定了三甲醇丙烷-季戊四醇(摩尔比60:40)固体溶液的相变热参数和热容。

关键词: 三甲醇丙烷, 季戊四醇, 热容, 相变焓

Abstract: The heat capacity of the solid solution of trimethylolpropane and pentaerythritol(60:40 mol%)was measured by means of an automated adiabatic calorimeter. A solid-solidtransition and a melting transition of the solid solution were found at 330.51 K and433.0 K with the transition enthalpies of 9.72 and 5.76 kJmol^-1, respectively.

Key words: trimethylolpropane, pentaerythritol, heat capacity, phase transition enthalpy

张志英, 杨孟林. 三甲醇丙烷-季戊四醇固体溶液的热容和相变焓[J]. 应用化学, 1990, 0(1): 88-90.

Zhang Zhiying, Yang Menglin. HEAT CAPACITY AND PHASE TRANSITION ENTHALPY OF TRIMETHYLOLPROPANE-PENTAERYTHRITOL SOLID SOLUTION[J]. Chinese Journal of Applied Chemistry, 1990, 0(1): 88-90.

[1]	朱德钦, 生瑜, 郑守扬, 童庆松. 三聚氰胺聚磷酸盐/季戊四醇配比、协效剂组及表面改性对聚丙烯基木塑复合材料的膨胀阻燃影响[J]. 应用化学, 2019, 36(6): 649-657.
[2]	周彦芳,曾泽,谢刚,焦晨婕,周玉炳,钟荣. 季戊四醇四苯甲酰甲酸酯的合成及光引发性能[J]. 应用化学, 2018, 35(6): 652-658.
[3]	迟咏梅, 徐松杰, 曹玉廷, 董坚. 新型两亲性聚酰胺的合成及性质[J]. 应用化学, 2017, 34(3): 269-275.
[4]	何建云, 黄洁, 宋纪蓉, 赵毅莎, 马聪, 徐抗震. N-(乙氧酰基)-N’-(2,4-二硝基苯胺基)硫脲的合成、晶体结构、比热容及热力学性质[J]. 应用化学, 2013, 30(07): 782-788.
[5]	刘畅, 褚劲松, 邵传强, 杨兴钰. 2,4,8,10-四氧杂-3,9-二磷杂螺环[5.5]十一烷-3,9-二氧-3,9-二取代苯甲醛腙的合成及其阻燃性能[J]. 应用化学, 2007, 24(7): 818-822.
[6]	孙才英, 李斌, 张转芳, 邵博, 徐树财. 季戊四醇螺环磷酸苯酚酯的合成及结构表征[J]. 应用化学, 2006, 23(2): 165-168.
[7]	谢红卫, 李滨耀. 酞侧基聚芳醚酮的热学性能[J]. 应用化学, 1996, 0(6): 95-97.
[8]	陈尔凡, 肖毅, 徐新. 季戊四醇酯难燃绝缘油的研究[J]. 应用化学, 1996, 0(2): 61-63.
[9]	赵小明, 刘志刚, 陈钟颀. 丁苯橡胶合成用活化剂乙二胺四乙酸盐溶液比热容的测定[J]. 应用化学, 1995, 0(1): 88-90.
[10]	王官武, 袁先友, 雷学工, 刘有成. 季戊四醇双缩醛的合成[J]. 应用化学, 1994, 0(1): 114-115.
[11]	朱国安, 郑吉民. 用DSC直接法测量POM晶体的比热容[J]. 应用化学, 1993, 0(5): 97-98.

三甲醇丙烷-季戊四醇固体溶液的热容和相变焓

HEAT CAPACITY AND PHASE TRANSITION ENTHALPY OF TRIMETHYLOLPROPANE-PENTAERYTHRITOL SOLID SOLUTION

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 11

编辑推荐

Metrics

本文评价