双酚F型聚酰亚胺薄膜的制备与性能

李媛1,李桂娟1,丁孟贤2,3,王震3*   

  1. (1.长春工业大学化学工程学院 长春；2.长春高琦聚酰亚胺材料有限公司 长春；
    3.中国科学院长春应用化学研究所 长春 130022)
  • 收稿日期:2010-12-23 修回日期:2011-04-11 出版日期:2011-12-10 发布日期:2011-12-10
  • 通讯作者: 王震，研究员; Tel:0431-85262737; Fax:0431-85262682; E-mail:wangzhen@ciac.jl.cn; 研究方向：聚酰亚胺材料
  • 基金资助:
    国家重点基础研究发展计划（2010CB631100）和吉林省科技发展计划项目（20080110）资助

Preparation and Performance of Bisphenol F-Type Polyimides Film

LI Yuan1, LI Guijuan1, DING Mengxian2,3, WANG Zhen3*   

  1. (1.School of Chemical Engineering,Changchun University of Technology,Changchun；
    2.The Company of Gaoqi Polyimides Material,Changchun;
    3.Changchun Institute of Applied Chemistry,Chinese Academy of Sciences,Changchun 130022)
  • Received:2010-12-23 Revised:2011-04-11 Published:2011-12-10 Online:2011-12-10

PDF

1771

被引次数

2 | 1

摘要：

以4-氯代酞酰亚胺和双酚F为原料，在N,N′-二甲基乙酰胺溶剂中，经水解、酸化、脱水，合成了一种新型的双酚F型二酐(BPFDA)单体，并用1H NMR和IR测试方法确认了其结构。 采用传统的一步法，用N,N′-二甲基乙酰胺作溶剂，BPFDA分别与4,4′-二氨基二苯醚（ODA）和4,4′-二氨基二苯甲烷（MDA）聚合，得到聚酰胺酸，并进一步热亚胺化得到聚酰亚胺薄膜，并对其进行了表征。 结果表明，BPFDA/ODA薄膜和BPFDA/MDA薄膜的玻璃化转变温度分别为200和204 ℃； 热失重分析表明，质量损失5%的温度分别为506.50和459.10 ℃；其拉伸强度分别为110和100 MPa。

关键词: BPFDA, 聚酰亚胺, 热性能, 力学性能。

Abstract:

A novel bisphenol F-type dianhydride(BPFDA) monomer was synthesized using 4-chlorophthalimide through hydration, acidification, and dehydration. Its structure was determined with 1H NMR and IR. Two types of polyimide films were prepared with the dianhydride and 4,4′-diaminodiphenyl ether(ODA) or 4,4′-methylene dianiline(MDA) via conventional one-step method in N,N′-dimethylacetamide. The obtained polyamic acid was then further imidized into polyimide films and characterized. Results show that the glass-transition temperatures of the polyimide films were 200 and 204 ℃；the temperatures of 5% mass loss were 506.50 and 459.10 ℃； and the tensile strength of the films were 110 and 100 MPa, respectively.

Key words: BPFDA, Polyimide, Thermal property, Mechanical properties.